Accelerated pavement testing (APT) is an effective testing procedure to evaluate asphalt pavements. With APT it is possible to determine and measure the structural response and pavement performance under a controlled, accelerated damage accumulation in a compressed period of time. However, different types of APT technologies can lead to different results. Full-size loading devices simulate road traffic accurately, but are expensive, while down-scaled size simulators are cost effective, nevertheless further away from reality. In this work, two types of APT mobile load simulators with different loading characteristics are compared with respect to pavement response in the field and in the laboratory. The MLS10 is a full-size simulator, whereas the MMLS3 is a one-third scale device. The relationship between the devices was studied in terms of the measured strains induced by both machines in the same pavement. Therefore, a testing field was instrumented with strain gauges and first trafficked with MLS10. Later, a slab of the instrumented pavement was cut off the road and tested in the laboratory with the smaller MMLS3. Furthermore, the structure of the pavement was modelled with a viscoelastic finite element method model and the moving loads of both machines were simulated considering size, speed and approximate footprints of their tires. As for the pavement materials, the properties of the different asphalt layers were determined in the laboratory. Experimentally acquired strain data were used to validate the models. Stress fields under different loading and environmental conditions were analysed and compared. The evaluation shows that the models can predict the pavement response under different loading conditions. However, they still need to be improved to increase the accuracy under different conditions. Further, the analysis of the strains show that both load simulators induce a different stress–strain situation and scaling of the pavement should be considered.

This paper reports part of an international research project with the long-term aim of developing more sustainable asphalt mixture with crack-healing properties by the addition of recycled metallic waste from industrial sources. Specifically, this article presents an evaluation of the physical, thermophysical, and mechanical properties of asphalt mixtures with metallic fiber obtained from recycled tires for crack-healing purposes. Detailed results on the crack-healing of asphalt mixtures will be reported in a second article. Results showed a small reduction on the bulk density and increase in the air voids content was quantified with increasing fiber contents. The experimental results showed that mixing and compaction was more difficult for higher fiber contents due to less space for the bitumen to freely flow and fill the voids of the mixtures. Computed tomography (CT) results allowed to identify clustering and orientation of the fibers. The samples were electrically conductive, and the electrical resistivity decreased with the increase of the fiber content. Fiber content had a direct effect on the indirect tensile stiffness modulus (ITSM) and strength (ITS) that decreased with increasing temperature for mixtures and with increase in fiber content. However, the indirect tensile strength ratio (ITSR) was within acceptable limits. In short, results indicate that fibers from recycled tires have a potential for use within asphalt mixtures to promote crack-healing.