Ammonia nitrogen wastewater (about 100 mg/L) was treated by two-stage ozone oxidation method. The effects of ozone flow rate and initial pH on ammonia removal were studied, and the mechanism of ammonia nitrogen removal by ozone oxidation was discussed. After the primary stage of ozone oxidation, the ammonia removal efficiency reached 59.32% and pH decreased to 6.63 under conditions of 1 L/min ozone flow rate and initial pH 11. Then, the removal efficiency could be over 85% (the left ammonia concentration was lower than 15 mg/L) after the second stage, which means the wastewater could have met the national discharge standards of China. Besides, the mechanism of ammonia removal by ozone oxidation was proposed by detecting the products of the oxidation: ozone oxidation directly and ·OH oxidation; ammonia was mainly transformed into NO₃⁻-N, less into NO₂⁻-N, not into N₂.

Parameters, such as inorganic ions and pH have different effects on the photocatalytic removal of X-3B and RhB using La/Bi₂WO₆.

La/Fe/TiO₂ composite photocatalysts were synthesized by Sol-Gel method and well characterized by powder X-ray diffraction (XRD), scanning electron microscopy (SEM), nitrogen-physical adsorption, and UV-Vis diffuse reflectance spectra (UV-Vis DRS). It is interesting that the doped catalysts were in anatase phase while the pure TiO₂ was in rutile phase. In addition, the composites possessed better physical chemical properties in photocatalytic activity than pure TiO₂: stronger visible-light-response ability, larger specific surface area, and more regular shape in morphology. The photodegradation results of ammonia nitrogen indicate that: the La/Fe/TiO₂ had higher catalytic activity to ammonia nitrogen waste water compared pure TiO₂ and the other single metal-doped TiO₂. pH 10 and 2 mmol/L H₂O₂ were all beneficial to the removal of ammonia nitrogen by La/Fe/TiO₂. However, the common inorganic ions of Cl⁻, NO₃⁻, SO₄²⁻, HCO₃⁻/CO₃²⁻, Na⁺, K⁺, Ca²⁺ and Mg²⁺ in water all inhibited the degradation of ammonia nitrogen. By balance calculation, at least 20% of ammonia nitrogen was converted to N₂ during the 64.6% removal efficiency of ammonia nitrogen.

Rare earth element La-doped TiO₂ (La/TiO₂) was synthesized by the sol-gel method. Benzohydroxamic acid was used as the objective pollutant to investigate the photocatalytic activity of La/TiO₂. The physicochemical properties of the prepared materials were characterized by X-ray diffraction, X-ray photoelectron spectroscopy, UV-vis diffuse reflectance spectroscopy, specific surface area and porosity, scanning electron microscopy and transmission electron microscopy. As a result, the doping of La could inhibit the crystal growth of TiO₂, increase its specific surface area and expand its response to visible light, thus improving its photocatalytic activity. La/TiO₂ with the doping ratio of 0.75% calcined at 500 °C, showing the highest photocatalytic activity to degrade benzohydroxamic acid under the irradiation of 300 W mercury lamp. About 94.1% of benzohydroxamic acid with the original concentration at 30 mg·L⁻¹ was removed after 120 min in a solution of pH 4.4 with an La/TiO₂ amount of 0.5 g·L⁻¹. Furthermore, 88.5% of the total organic carbon was eliminated after 120 min irradiation. In addition, after four recycling runs, La/TiO₂ still kept high photocatalytic activity on the photodegradation of benzohydroxamic acid. The interfacial charge transfer processes were also hypothesized.