Based on aqueous poly(vinyl alcohol) (PVA) solutions with different content of polymer having different molecular masses and chain tacticity, macroporous viscoelastic gels (PVA cryogels) are prepared in various regimes of freezing-storage in a frozen state-thawing. Shear modulus and fusion temperature of corresponding samples are measured; the structure of thin sections is studied by optical microscopy and the images are processed and analyzed. It is shown that the rigidity and heat endurance of cryogels rise with an increase in the concentration of initial PVA solution and a decrease in the rate of thawing. The influence of the temperature of cryogenic treatment and the PVA molecular mass has an extreme character. At the same time, the effect of the main parameters of cryotropic gelation on the macroporous morphology of PVA cryogels is manifested in the form of more complex dependences because of its multiple-factor character. Therefore, distinct structure-property correlations are not observed in many cases. Cluster analysis of the morphometric characteristics of cryogels in comparison with data on their rigidity makes it possible to classify these systems.

Poly(vinyl alcohol) cryogels are obtained and investigated. The cryogels are prepared by freezing an initial polymer solution (100 g/L) at chilling rates of 1.85, 0.3, 0.03, or 0.003°C/min followed by defrosting the frozen (−20°C/12 h) preparations at heating rates of 0.3, 0.03, or 0.003°C/min. It is shown that a noticeable influence of the chilling rate on the rigidity and heat endurance of the gel matrix is observed at very slow regimes of chilling (on the order of thousandths of degree centigrade per minute). One of the reasons for a reduction in the rigidity of resulting cryogels and the fusion enthalpy of the nodes in their supramolecular networks is the formation of a homo-phase hydrogel during the long-term exposure of the concentrated polymer solution to low temperatures prior to the onset of ice crystallization. The effect of the regime of chilling the polymer solution being frozen on the porous structure of cryogels resulting from the thawing of the preparations is ambiguous due to the multifactor character of this effect; therefore, in many cases, well-defined structure-property correlations are not observed.

Macroporous viscoelastic poly(vinyl alcohol) (PVA) cryogels were prepared from aqueous PVA solutions containing additives (0–1.2 mol/l) of alkali metal chlorides (LiCl, NaCl, KCl, CsCl) by cryogenic treatment (freezing at −20°C for 12 h and subsequent thawing at a rate of 0.03°C/min). Shear moduli and fusion temperatures of corresponding samples were determined and the structure of thin sections was studied by optical microscopy with subsequent processing and analysis of images obtained. It was shown that the rigidity, heat endurance, and mean pore sizes of formed cryogels monotonically decrease with increasing content of chaotropic lithium chloride. In the case of other three salts, the dependences of rheological characteristics of cryogels on the concentration of low-molecular-weight electrolyte were extreme due to the competition between factors that promote and prevent PVA cryotropic gelation. At the same time, fusion temperatures of gel samples increased steadily with increasing content of these salts. Microscopic studies revealed substantial (by factor of two to three) decrease in macropore sizes even at low content of salt compared to mean cross sections of pores in cryogel containing no additive; morphometric analysis of obtained images makes it possible to reveal the linear correlations between the rheological characteristics of cryogels formed in the presence of LiCl and the sizes of their macropores.