Currently, the inappropriate disposal of plastic materials, such as polyethylene terephthalate (PET) wastes, is a major environmental problem since it can cause serious damage to the environment and contribute to the proliferation of pathogenic microorganisms. To reduce this accumulation, PET-type bottles have been recycled, and also explored in other applications such as the development of membranes. Thus, this research aims to develop electrospun microfiber membranes from PET wastes and evaluate their use as an air filter media. The solution concentrations varied from 20 to 12% wt% of PET wastes, which caused a reduction of the average fiber diameter by 60% (from 3.25 µm to 1.27 µm). The electrospun filter membranes showed high mechanical resistance (4 MPa), adequate permeability (4.4 × 10⁻⁸ m²), high porosity (96%), and provided a high collection efficiency (about 100%) and low-pressure drop (212 Pa, whose face velocity was 4.8 cm/s) for the removal of viable aerosol nanoparticles. It can include bacteria, fungi, and also viruses, mainly SARS-CoV-2 (about 100 nm). Therefore, the developed electrospun membranes can be applied as indoor air filters, where extremely clean air is needed (e.g., hospitals, clean zones of pharmaceutical and food industry, aircraft, among others).

The development of α and β-phases and the molecular orientation of injection molded disks of two isotactic polypropylene (i-PP) resins were studied by wide angle X-ray diffraction (WAXD) and pole figures. A nucleated (NPP) and non-nucleated (HPP) polymers were analyzed. The main proposal of this article was the comprehensive study of the interrelations between the processing conditions, phase contents and PP α-phase molecular orientation of injection molded PP resins. In both resins, it was observed that the α-phase was present in all regions along the thickness while the β-phase was present mainly in the external layers, decreasing from the surface to the core; however this last phase was present in a very small amount in the NPP resin. For both polymers, the orientation of the macromolecules c-axis was higher along the flow direction (RD) than along the transverse direction (TD). The b-axis of the PP α-phase molecules was oriented to the thickness direction (ND). The orientation of the c-axis along RD and b-axis along ND of the NPP samples was considerably higher than of the HPP samples, due to the NPP faster crystallization kinetics. For both polymers, the most influential processing parameters on the molecular orientation were the mold temperature and flow rate. The results indicate that, as the mold temperature increased, the characteristic molecular orientation of PP α-phase, with c-axis along RD and b-axis along ND, decreased. With increase in the flow rate an increase of the c-axis molecular orientation of the samples along RD was observed

Mantas não tecidas de nanofibras de três polímeros biodegradáveis poli(ácido láctico), PDLLA, poli(Ε-caprolactona), PCL, e poli(butileno adipato-co-tereftalato), PBAT e seus nanocompósitos com uma nanoargila montmorilonita (MMT) foram produzidas por eletrofiação. A morfologia, o comportamento térmico e a estrutura interna das nanofibras foram analisados por microscopia eletrônica de varredura e transmissão, calorimetria diferencial de varredura e difração de raios X, respectivamente. Observou-se que as nanofibras dos nanocompósitos possuíam diâmetros menores do que os correspondentes polímeros puros e que as nanofibras de PBAT puro e de PBAT/MMT apresentavam a menor cristalinidade de todas as mantas. A viabilidade celular de todas as nanofibras foi analisada pela técnica de redução do sal de tetrazolium pelo complexo enzimático piruvato desidrogenase presente na matriz de mitocôndrias (teste MTT). Os resultados mostraram que nenhuma manta nanofibrílica apresentou toxicidade às células e que as nanofibras de PBAT puro e seu nanocompósito propiciaram ainda um ambiente mais favorável ao desenvolvimento celular de fibroblastos de cardiomiócitos do que as condições oferecidas pelo controles, provavelmente por apresentarem menores diâmetros e baixa cristalinidade em relação às demais nanofibras. Estes resultados mostram o potencial de uso destas mantas nanofibrílicas como suportes de crescimento celular.