The presented study is focused on optimization and characterization of a high-alumina refractory aggregate based on natural raw materials—kaolins, claystone, and mullite dust by-product (used to increase the alumina and mullite contents, respectively). In total, four individual formulas with the Al₂O₃ contents between 45 and 50 wt.% were designed; the samples were subsequently fired, both in a laboratory oven and an industrial tunnel furnace. The effects of repeated firing were examined during industrial pilot tests. Mineral and chemical compositions and microstructures, of both the raw materials and designed aggregates, were thoroughly investigated by the means of X-ray fluorescence spectroscopy, powder X-ray diffraction, and optical and scanning electron microscopies. Porosity, mineral composition, and mullite crystal-size development during the firing process were also studied. Based on the acquired results, the formula with the perspective to be used as a new mullite grog, featuring similar properties as the available commercial products, however, with reduced production expenses, was selected. The quality of grog determines to a large extent the properties of the final product. Hence, optimization of aggregates for specific refractories is of a great importance. The production of engineered aggregates provides the opportunity to utilize industrial by-products.

Colloidal bonds are realized by sol–gel technology. The binder system of the refractory castable belongs to the Al₂O₃–SiO₂ binary diagram. Mullite is the most thermally stable mineral in this system. This work was motivated by an attempt to maximize the mullite content in the NCC binder system, because a high content of mullite is a guarantee of the long service life of refractories. Initially, the mineralogical composition of the pure gel was tested after drying and firing at temperatures between 1000 °C and 1600 °C. The behavior of the gel during drying was described. Subsequently, a method of minimizing gel shrinkage during drying was sought. To this aim, fine fillers (microfillers) of alumina and silica were tested. In particular, the reactivity of the microfillers, the ability of the microfillers to react with the sol to form mullite, and the drying shrinkage of the microfiller-doped gel were evaluated. The study showed that the least suitable source of Al₂O₃ in terms of its reactivity is tabular corundum, which produces the lowest amount of mullite. The internal structure of the prepared binder system when using different microfillers was described. Based on the results from the second stage of the work, several complete matrixes of the binder system were designed and the degree of their mullitization at different firing temperatures was studied. During this stage, it was shown that the degree of mullitization of the binder system depends mainly on the microsilica content. In the binder system, the maximum mullite content recorded was 76%. The effect of amorphous SiO₂ on the bulk density and internal structure of the binder system was also described.

Colloidal silica is used in many kinds of industry. It is an aqueous dispersion of SiO₂ nanoparticles. SiO₂ colloidal solutions are commercially available in different concentrations, with different particle sizes and are stabilized with different ions. Colloidal SiO₂ was used in this study as a cement replacement in refractory castable. The present study, in its first stage, offers an assessment of five different SiO₂ colloidal solutions. The particle size of the solutions was 15 nm, the particle concentration was 30% and 40% and the colloidal solutions were stabilized with Na⁺, OH⁻ and Cl⁻ ions. The effect of the colloidal solutions on selected characteristics of the refractory pastes and on their mineralogical composition after firing at 1000 °C and 1500 °C was described. The most suitable SiO₂ colloidal solution from the first stage was subsequently used for the refractory castable test samples’ preparation in the second stage. Refractory castables, unlike paste, contain a coarse aggregate (grog) up to a grain size of 6 mm. Four types of coarse refractory grog were evaluated. Their effect on selected characteristics of the refractory castable and on its mineralogical composition after firing at 1000 °C and 1500 °C was described. The selected characteristics, within the scope of this study, include bulk density, apparent porosity, cold modulus of rupture and linear changes after firing. Finally, the study describes the effect of the sol particle concentration and the effect of pore size distribution on corrosion resistance and on the internal structure of the material. Mineral and chemical compositions and microstructures of both the raw materials and designed aggregates were thoroughly investigated by the means of X-ray fluorescence spectroscopy, powder X-ray diffraction and scanning electron microscopy. An analysis of the transition zone between corrosive media (K₂CO₃) and tested castables showed better corrosion resistance for a sol-gel castable than an ultra-low cement castable.

High alumina ceramics is a part of the refractory ceramics in SiO₂-Al₂O₃ binary system. The aim of this paper is to characterize the effect of ageing raw materials and its influence on final properties of fired refractory grog. Refractory grog is very important component in production of refractory materials, such as fireclay, mullite and andalusite bricks. Refractory grog is manufactured generally from clay, claystone and kaolin, nowadays is mainly burnt in rotary and shaft kilns. The primary objective of this article is to determine an influence of ageing effect, which has impact on mineralogical composition of raw material which obviously results in different mineralogical composition of fired grog. Raw material with different age was used for the mixtures and properties of fired samples were investigated, considering the influence of the raw materials mixtures. Specifically, the apparent porosity, water absorption, bulk density, apparent porosity, mineralogical composition and pore distribution were investigated.

This paper deals with sol-gel process and application in no cement castables based on andalusite. The use of calcium free binder increases the refractory parameters of material and allows its faster drying. Six colloidal sols from CWK Bad Köstritz based on SiO₂ were tested, which differed not only in concentration and particle size, but also in pH. The influence of silica sols on the consistency of fresh castable, initial setting and final setting times were investigated. Furthermore, basic parameters after firing, such as bulk density, apparent porosity, flexural and compressive strength, were tested.

Lightweight refractory materials are most used as a second layer in the lining. Many techniques can be used to their production depending on their final application. This manuscript is focused on utilization of sol-gel method as the replacement of hydraulic or ceramic bond in the manufacturing process of grog and castable preparation. The results show possible ways to produce high quality lightweight refractory grog with very high purity and also lightweight refractory castable, which performs good results in terms of bulk density, apparent porosity, cold crushing strength, cold modulus of rupture and permanent linear changes.