The aim of this review was to analyze/investigate the synthesis, properties, and applications of polyvinyl alcohol–halloysite nanotubes (PVA–HNT), and their nanocomposites. Different polymers with versatile properties are attractive because of their introduction and potential uses in many fields. Synthetic polymers, such as PVA, natural polymers like alginate, starch, chitosan, or any material with these components have prominent status as important and degradable materials with biocompatibility properties. These materials have been developed in the 1980s and are remarkable because of their recyclability and consideration of the natural continuation of their physical and chemical properties. The fabrication of PVA–HNT nanocomposites can be a potential way to address some of PVA’s limitations. Such nanocomposites have excellent mechanical properties and thermal stability. PVA–HNT nanocomposites have been reported earlier, but without proper HNT individualization and PVA modifications. The properties of PVA–HNT for medicinal and biomedical use are attracting an increasing amount of attention for medical applications, such as wound dressings, drug delivery, targeted-tissue transportation systems, and soft biomaterial implants. The demand for alternative polymeric medical devices has also increased substantially around the world. This paper reviews individualized HNT addition along with crosslinking of PVA for various biomedical applications that have been previously reported in literature, thereby showing the attainability, modification of characteristics, and goals underlying the blending process with PVA.

Due to current trend and increasing interest towards natural based fiber products, Kenaf (Hibiscus cannabinus) fibers have been used for the developments of many products. Therefore, Kenaf fiber-reinforced composites have been widely used in engineering and industrial applications. The present work deals with the fabricating and characterization of untreated and treated kenaf/polypropylene (PP)-reinforced composites. Composites of PP reinforced with treated and untreated kenaf fibers were fabricated using the injection molding technique. Different fiber loadings of 10, 20, 30, 40, 50 wt% treated and untreated kenaf composites were also prepared. X-ray diffraction (XRD), scanning electron microscopy (SEM), Fourier transform infrared (FTIR) spectroscopy and thermo gravimetric analysis (TGA) were performed on the treated, untreated kenaf fibers and kenaf/PP composites. Moreover, the alkaline-treated kenaf composites exhibit better physical, morphological, and mechanical properties because of the compatibility of kenaf with PP. However, variations in tensile and flexural properties depend on treatment and kenaf fiber contents. The percentage increase in the mechanical properties of the treated kenaf/PP composites relative to that of PP was also measured. In addition, 40 wt% kenaf fiber loading resulted in higher mechanical properties. By contrast, kenaf/PP composite with 50% fiber loading was not successfully prepared because of improper mixing and the burning of kenaf fibers in the PP matrix. To conclude, 40% kenaf/PP composites with superior physical and mechanical properties may be used in variety of applications such as automotive, sports, construction, animal bedding, and mass production industries