The gel of zeolite NaY has potential as a precursor of other zeolites. The particular interest in this work is to convert the gel of NaY to NaP2. We found that the pure phase NaP2 can be produced simply by the conventional hydrothermal (CH) method at 150 °C for 24 h. This NaP2 sample, named CH150, has an average particle size of 10.3 µm and an Si/Al ratio of 1.82. In the case of single crystallization via microwave-assisted hydrothermal (MH) method, various parameters were studied, including the crystallization temperature (90, 150, 175 °C) and time (15, 30, 45, 60 min). The samples were analyzed by X-ray diffraction and scanning electron microscopy. However, mixed phases of P1 and P2 or ANA were obtained from all samples. Another attempt was made by a double crystallization via MH method as followed: at 90 °C for 1 h, quickly cooled down to room temperature in the microwave chamber and aged for 23 h, and finally at 150 °C for 1 h. The sample, named MH90A150, has an average crystal size of 16.45 µm and an Si/Al ratio of 1.85. The high Al content of NaP2 in both samples (CH150 and MH90A150) could lead to interesting applications.

The goal of this work is to synthesize zeolite NaY inside Lead tree wood. The wood is mixed with zeolite seed gel before mixing with feed gel and subsequent hydrothermal treatment. In the first trial, the dried and untreated Lead tree wood is mixed with the gel of zeolite NaY before the hydrothermal process. Only zeolite NaP is produced. Then, sonication is applied to the wood and zeolite gel mixture before the hydrothermal process. The product is mixed with the phase of NaP and NaY. In the next attempt, the wood is treated with acid reflux before mixing with the zeolite seed gel. NaY is successfully produced inside the wood. When sonication is also applied, the amount of NaY is increased. The presence of zeolites in the wood are confirmed by X-ray diffraction, scanning electron microscopy, nitrogen adsorption, and thermogravimetric analysis. Moreover, the composites are tested for the adsorption of nickel (II) ions from aqueous solutions. The novel Lead tree wood-zeolite NaY composite has the potential as an adsorbent which could be separated easily from the liquid media.

Zeolite NaY synthesized from a typical procedure could suffer from agglomeration. Adding non-refluxed cogon grass (NG) to the synthesis gel could produce NaY with good dispersion and uniform crystal size. Small molecules produced from cogon grass in alkaline conditions could prevent agglomeration. The obtained zeolite (Y-NG) has a crystallinity and surface area comparable to the synthesis without grass (Y-WG). Y-NG demonstrated similar paraquat adsorption capacity to Y-WG at high initial concentrations. On the other hand, the zeolite from the addition of acid-refluxed grass (Y-RG) has the lowest crystallinity, smallest surface area, and poorest paraquat adsorption capacity. The effect of grass amount on the zeolite structure was studied. One gram of cogon grass was the optimum amount to add to the synthesis gel.