Under normal conditions, the cross-sections of reinforced concrete in classic skeleton construction systems are often only partially loaded. This contributes to non-sustainable construction solutions due to an excess of material use. Novel cross-disciplinary workflows linking architects, engineers, material scientists and manufacturers could offer alternative means for more sustainable architectural applications with extra lightweight solutions. Through material-specific use of plant-based Natural Fiber-Reinforced Polymer Composites (NFRP), also named Biocomposites, a high-performance lightweight structure with topology optimized cross-sections has been here developed. The closed life cycle of NFRPs promotes sustainability in construction through energy recovery of the quickly generative biomass-based materials. The cooperative design resulted in a development that were verified through a 1:10 demonstrator, whose fibrous morphology was defined by biomimetically-inspired orthotropic tectonics, generated with by the fiber path optimization software tools, namely EdoStructure and EdoPath in combination with the appliance of the digital additive manufacturing technique: Tailored Fiber Placement (TFP).

Fiber Reinforced Polymers (FRPs) are increasingly popular building materials, mainly because of their high strength to weight ratio. Despite these beneficial properties, these composites are often fabricated in standardized mass production. This research aims to eliminate costly molds in order to simplify the fabrication and allow for a higher degree of customization. Complex three-dimensional shapes were instead achieved by a flat reinforcement, which was resin infused and curved folded into a spatial object before hardening. Structural stability was gained through geometries with closed cross-sections. To enable this, the resource-saving additive fabrication technique of tailored fiber placement (TFP) was chosen. This method allowed for precise fibers’ deposition, making a programmed anisotropic behavior of the material possible. Principles regarding the fiber placement were transferred from a biological role-model. Five functional stools were produced as demonstrators to prove the functionality and advantages of the explained system. Partially bio-based materials were applied to fabricate the stool models of natural fiber-reinforced polymer composites (NFRP). A parametric design tool for the global design and fiber layout generation was developed. As a result, varieties of customized components can be produced without increasing the design and manufacturing effort.

A suitable functionalization of graphene and its derivatives can further enhance the material properties of nanocomposites. In contrast to chemical functionalization methods that have been extensively researched, functionalization by plasma treatment is relatively unexplored. In this work, we compare the mechanical, thermal and electrical characteristics of an epoxy matrix incorporating loadings from 0.00 to 1.50 wt% of non-functionalized (rGO) and amine-functionalized reduced graphene oxide (frGO) for which the functionalization is realized by plasma processing. No significant difference between the rGO- and frGO-including nanocomposites was observed with respect to the stiffness, strength, specific heat capacity, coefficient of thermal expansion and electrical conductivity. Yet, the composites with 1.50 wt% frGO (rGO) exhibited a thermal conductivity that was 27% (20%) higher than the neat polymer due to the enhanced interface, which enabled a better transfer of heat. In addition, a considerable increase in the specific heat capacity and thermal conductivity was established with rising temperatures. This information will facilitate the choice of materials depending on the loading and functionalization of graphene materials for composite applications with an epoxy matrix.

This study evaluates the effect of plasma surface functionalization of reduced graphene oxide particles on the processing characteristics and homogeneity of dispersion of a bisphenol A‐(epichlorhydrin) epoxy matrix and amine‐based hardener with varying weight fractions from 0.00 to 1.50 wt%. It was observed that amine‐functionalized reduced graphene oxide leads to a more drastic viscosity increase of up to 18‐fold of the uncured suspensions and that its presence influences the conversion rates of the curing reaction. Optical microscopy of thin sections and transmission electron microscopy analysis showed that a more homogeneous dispersion of the particles could be achieved especially at higher weight fractions by using an appropriate surface functionalization. This knowledge can be used to define suitable processing conditions for epoxies with amine‐based hardeners depending on the loading and functionalization of graphene‐related particles.

Within the dry fibre placement (DFP) process, spread and pre-bindered carbon fibre rovings are automatically processed into dry textile preforms using 2-D and 3-D laying systems. The aim was to automate existing hand lay-up processes, reducing the complexity, increasing robustness, and facilitating the handling of the DFP technology. Process reliability, low waste rates, and flexible production are demonstrated. In this publication, the influences of the process parameters, 2 mm wide gaps and the percentage of 90° plies in the laminate, are investigated with regard to the mechanical properties, the permeability, and the infusion times in the preform z-direction (thickness). The effects on stiffness and strength are compared for several use cases. An approach to determine the infusion times as a function of the laminate thickness, the ply structure, and 2 mm wide gaps is demonstrated and analysed using vacuum-assisted process (VAP) infusion tests. The investigations are performed with carbon fibre tows (24 k), a reactive epoxy-based binder system, and a thermoset infusion resin system.