Through a straightforward approach, a new meltable, halogen-free, nitrogen-phosphorus-based flame retardant (FR), 6-(2-(4,6-diamino-1,3,5-triazin-2-yl)ethyl) dibenzo[c,e][1,2]oxaphosphinine 6-oxide (DTE-DOPO) was synthesized and incorporated in polyamide 6 (PA6). It was proved that a very low phosphorus content of 1.46 wt% for DTE-DOPO additive improved the flame retardancy of PA6, leading to a non-flammable material. The performance of the new additive was compared to that of the commercially-available Exolit^® OP 1230. The PA6 formulations were evaluated by measuring the rheological, mechanical, and flammability behavior. Using compounding by melt extrusion, 17 wt% additives was introduced into PA6 matrix and the corresponding formulations were characterized. The results evidenced a higher homogeneity of DTE-DOPO with PA6, a high thermal stability with a catalyzing decomposition effect on PA6 caused by the presence of the new developed FR, enhanced elasticity for the PA6/DTE-DOPO formulation and a V0 rating for both formulations. Thermal and fire analysis indicated a primary gas-phase activity, combined with a complete suppression of the self-sustained burning for the PA6/DTE-DOPO formulation.

A study was carried out involving the filling of epoxy resin (EP) with bentonites and silica modified with polyhedral oligomeric silsesquioxane (POSS). The method of homogenization and the type of filler affect the functional and canceling properties of the composites was determined. The filler content ranged from 1.5% to 4.5% by mass. The basic mechanical properties of the hybrid composites were found to improve, and, in particular, there was an increase in tensile strength by 44%, and in Charpy impact strength by 93%. The developed hybrid composites had characteristics typical of polymer nanocomposites modified by clays, with a fine plate morphology of brittle fractures observed by SEM, absence of a plate separation peak in Wide Angles X-ray Scattering (WAXS) curves, and an exfoliated structure observed by TEM.

One-part, moisture curing polyurethane (PUR) adhesives based on poly(oxypropylene)diol Rokopol® and 4,4’-diphenylmethylene diisocyanate (MDI) modified with di-isononyl phthalate and a number of inorganic fillers and additives such as carbon black, thixotropic agent, dispersants and dibutyltin dilaurate as curing catalyst were developed. Adhesive curing was followed using dynamic oscillation rheometry and effect of some components on viscoelastic properties of curing materials was discussed. The cured materials were characterized by means of differential scanning calorimetry (DSC) and water contact angle measurements. The adhesive performance of obtained materials in bonding aluminum was evaluated by tensile shear bond strength tests.