Respiration of Escherichia colicatalyzed either by cytochrome bo′ or bd is sensitive to micromolar extracellular NO; extensive, transient inhibition of respiration increases as dissolved oxygen tension in the medium decreases. At low oxygen concentrations (25–33 μm), the duration of inhibition of respiration by 9 μm NO is increased by mutation of either oxidase. Respiration of an hmp mutant defective in flavohemoglobin (Hmp) synthesis is extremely NO-sensitive (I₅₀ about 0.8 μm); conversely, cells pre-grown with sodium nitroprusside or overexpressing plasmid-bornehmp ⁺ are insensitive to 60 μm NO and have elevated levels of immunologically detectable Hmp. Purified Hmp consumes O₂ at a rate that is instantaneously and extensively (>10-fold) stimulated by NO due to NO oxygenase activity but, in the absence of NO, Hmp does not contribute measurably to cell oxygen consumption. Cyanide binds to Hmp (K _d 3 μm). Concentrations of KCN (100 μm) that do not significantly inhibit cell respiration markedly suppress the protection of respiration from NO afforded by Hmp and abolish NO oxygenase activity of purified Hmp. The results demonstrate the role of Hmp in protecting respiration from NO stress and are discussed in relation to the energy metabolism of E. coli in natural O₂-depleted environments.

We have demonstrated heterogeneous photocatalytic degradation of microcystin-LR (MC-LR) by visible light activated carbon doped TiO(2) (C-TiO(2)) nanoparticles, synthesized by a modified sol-gel route based on the self-assembly technique exploiting oleic acid as a pore directing agent and carbon source. The C-TiO(2) nanoparticles crystallize in anatase phase despite the low calcination temperature of 350 °C and exhibit a highly porous structure that can be optimized by tuning the concentration of the oleic acid surfactant. The carbon modified nanomaterials exhibited enhanced absorption in the broad visible light region together with an apparent red shift in the optical absorption edge by 0.5 eV (2.69 eV), compared to the 3.18 eV of reference anatase TiO(2). Carbon species were identified by x-ray photoelectron spectroscopy analysis through the formation of both Ti-C and C-O bonds, indicative of substitution of carbon for oxygen atoms and the formation of carbonates, respectively. Electron paramagnetic resonance spectroscopy revealed the formation of two carbon related paramagnetic centers in C-TiO(2), whose intensity was markedly enhanced under visible light illumination, pointing to the formation of localized states within the anatase band gap, following carbon doping. The photocatalytic activity of C-TiO(2) nanomaterials was evaluated for the degradation of MC-LR at pH 3.0 under visible light (λ > 420 nm) irradiation. The doped materials showed a higher MC-LR degradation rate than reference TiO(2), behavior that is attributed to the incorporation of carbon into the titania lattice.