Nickel (Ni) and cobalt (Co) are strategic metals that have found applications in a wide range of metallurgical and industrial uses. In this study, the dissolution of a mixed nickel–cobalt hydroxide precipitate using organic acids (citric, oxalic, and malic acid) was investigated. Citric acid was found to be the best leaching agent yielding the following dissolution rates: 91.2% Ni, 86.8% Co, and 90.8% Mn. Oxalic acid resulted in low dissolution, which is likely due to the formation of insoluble metal oxalates. The impact of acid concentration, leaching time, and temperature on metal dissolution was systematically examined. The optimal dissolution conditions were identified as 0.5 M citric acid at 30 °C for 30 min, utilizing a 1/20 solid/liquid ratio and a stirring speed of 400 revolutions per minute (rpm). The attempt to use oxidants, such as potassium permanganate (KMnO₄) and hydrogen peroxide (H₂O₂), to achieve selective dissolution in an organic acid environment was not successful, which was different from that in the sulfuric acid case. As for the leaching kinetics in the organic acids, it seems that the leaching of Ni correlates with the Shrinking Core Model, specifically regarding porous-layer diffusion control. Based on the experimental results, the activation energy for the leaching of Ni was estimated to be 3.1 kJ/mol.

The lithium-ion battery (LIB) thermal runaway (TR) emits a wide size range of particles with diverse chemical compositions. When inhaled, these particles can cause serious adverse health effects. This study measured the size distributions of particles with diameters less than 10 µm released throughout the TR-driven combustion of cylindrical lithium iron phosphate (LFP) and pouch-style lithium cobalt oxide (LCO) LIB cells. The chemical composition of fine particles (PM_2.5) and some acidic gases were also characterized from filter samples. The emission factors of particle number and mass as well as chemical components were calculated. Particle number concentrations were dominated by those smaller than 500 nm with geometric number mean diameters below 130 nm. Mass concentrations were also dominated by smaller particles, with PM₁ particles making up 81–95% of the measured PM₁₀ mass. A significant amount of organic and elemental carbon, phosphate, and fluoride was released as PM_2.5 constituents. The emission factor of gaseous hydrogen fluoride was 10–81 mg/Wh, posing the most immediate danger to human health. The tested LFP cells had higher emission factors of particles and HF than the LCO cells.