Pisha sandstone (PS) is a special interbedded rock in the middle reaches of the Yellow River that experiences severe weathering and is loose and broken. Due to severe multiple erosion events, the Pisha sandstone region is called “the most severe water loss and soil erosion in the world” and “the ecological cancer of the earth”. As a special pozzolanic mineral, PS has the potential to be used as precursors for the synthesis of green and low-carbon geopolymer gel materials and applied in ecological restoration. This paper aims to undertake a phase review of the precursors for geopolymer gel materials. The genesis and distribution, physical and chemical characterization, erosion characteristics, and advances in the ecological restoration of PS are all summarized. Furthermore, current advances in the use of PS for the synthesis of geopolymer gel materials in terms of mechanical properties and durability are discussed. The production of Pisha sandstone geopolymer gels through the binder jetting technique and 3D printing techniques is prospected. Meanwhile, the prospects for the resource application of PS in mine rehabilitation and sustainable ecology are discussed. In the future, multifactor-driven comprehensive measures should be further investigated in order to achieve ecological restoration of the Pisha sandstone region and promote high-quality development of the Yellow River Basin.

The Yellow River has the highest sediment concentration in the world, and the Yellow River coarse sediment mainly comes from a particular kind of argillaceous sandstone, Pisha sandstone. This paper reports an investigation of the possibility of development of low-cost engineering materials using Pisha sandstone via ion exchange modification. The effect of modifiers with different concentration on the inhibition of volume expansion and the strength enhancement of modified Pisha sandstone were studied via ion exchange solidification. The effects of the concentration of ten types of modifier solutions and curing age were considered. The hydration of the mineral components, particle surface potential and reaction products were studied, respectively, by XRD, zeta potential, TG/DTG and SEM. Expansion volume and shear strength tests were conducted to assess the volume stability and mechanical property of modified Pisha sandstone. It showed that the expansion of Pisha sandstone was controlled and that the volume stability and shear strength were improved via ion exchange modification. The results of XRD, TG/DTG and SEM showed that the spacing of the crystal layers of the Pisha sandstone clay mineral and the mass lost had decreased significantly. When the concentration of the modifier was 0.05 mol/L, the volume reduced by 54.55% maximum and the shear strength reached the peak of 138 kPa.