The cyclic oxidation response of Mo-14Hf-23B and Mo-14.8Zr-26B (compositions in at. %) was investigated in air at 800 °C, which is a critical temperature for Mo-based alloys because of the pesting phenomenon. Rapid oxidation was observed for the unprotected samples, and an oxidation protection coating was developed based on a preceramic polymer with silicon and boron as particulate fillers. Cyclic oxidation tests of the coated samples showed excellent oxidation protection: no Mo, Hf or Zr oxides were found after testing and a small mass gain in the initial stage of oxidation indicated the formation of a glassy protection layer on the alloys surfaces after exposure to air at 800 °C.

Oxidation barrier coatings on the base of a perhydropolysilazane precursor with different amounts of Si, B, SiB₆ and Mo₅SiB₂ (T2) fillers for the oxidation protection of Mo-Si-B alloys were developed. The influence of different filler compositions as well as the influence of pyrolysis conditions (temperature and atmosphere) was studied. The coating slurries were examined with respect to their rheological behavior, which allows optimization of the coating slurry. Dilatometry studies show that the coefficient of thermal expansion of the composites can be matched to refractory, especially molybdenum alloy based, substrates by varying the content and the composition of the filler. The pyrolyzed coating systems offer a low porosity, which is one of the key parameters to a high oxidation protection capability.