The presented study describes a method for the preparation and modification of cylindrical polyurethane structures with polyvinylpyrrolidone (PVP) hydrogel coating. The modified polyurethane scaffolds were fabricated using the phase-inversion technique and intended to be used as a vascular prosthesis. The proposed modification method involves a two-step Fenton-type reaction. Physicochemical analysis (Fourier transform infrared spectroscopy, scanning electron microscopy) confirmed the presence of the hydrogel coating. The influence of PVP and polymerization initiator (cumene hydroperoxide) concentrations on hydrogel's properties were examined. The higher concentrations of reagent were used, the thicker coating was obtained. After modification, the material's surface becomes more hydrophilic in comparison to pristine polyurethane. Cytotoxicity assay (MTT test) confirmed that PVP-coating is not toxic. The introduction of hydrogel coating resulted in a significant decrease in the fibrinogen adsorbed to the material's surface as compared to a non-modified polymer. Platelet adhesion assay demonstrated almost no platelet adhesion to the modified surfaces.

This paper presents a method for polyurethane surface functionalization for tissue engineering applications. Functionalization has been carried out by grafting acrylic acid to the polyurethane surface with the use of radical polymerization with a Ce⁴⁺ initiator. Contrary to other papers suggesting that the presence of hydroxyl groups are essential for successful grafting via ceric ions, we propose a method with the omission of the surface hydroxylation step. The influence of reaction conditions: reaction time, reaction temperature and monomer concentration on carboxyl groups surface density has been analyzed and described. The quantity of carboxyl groups on the surface was determined with the use of the TBO method. Materials grafted with acrylic acid have been subjected to conjugation with a peptide using sulfoNHS/ EDC chemistry. Successful incorporation of the peptide has been confirmed by an ELISA assay. Additionally, for better characterization, after each step of modification materials were subjected to SEM, FTIR-ATR, XPS and contact angle measurement analysis.

This study describes a method for the modification of polyurethane small-diameter (5 mm) vascular prostheses obtained with the phase inversion method. The modification process involves two steps: the introduction of a linker (acrylic acid) and a peptide (REDV and YIGSR). FTIR and XPS analysis confirmed the process of chemical modification. The obtained prostheses had a porosity of approx. 60%, Young’s Modulus in the range of 9–11 MPa, and a water contact angle around 40°. Endothelial (EC) and smooth muscle (SMC) cell co-culture showed that the surfaces modified with peptides increase the adhesion of ECs. At the same time, SMCs adhesion was low both on unmodified and peptide-modified surfaces. Analysis of blood-materials interaction showed high hemocompatibility of obtained materials. The whole blood clotting time assay showed differences in the amount of free hemoglobin present in blood contacted with different materials. It can be concluded that the peptide coating increased the hemocompatibility of the surface by increasing ECs adhesion and, at the same time, decreasing platelet adhesion. When comparing both types of peptide coatings, more promising results were obtained for the surfaces coated with the YISGR than REDV-coated prostheses.