Polyetherimide (PEI) is a widely applied as engineering plastic in the electronics, aerospace, and automotive industries but the disadvantages of extremely low conductivity, atmospheric moisture absorption, and poor fluidity at high temperature limits its application. Herein, commercial multi-walled carbon nanotubes (MWCNTs) were modified with a long alkyl chain molecule, octadecylamine (ODA), to produce a uniform dispersion in commercial PEI matrices. Both covalent and noncovalent modification of MWCNTs with ODA, were prepared and compared. Modified MWCNTs were incorporated in PEI matrices to fabricate nanocomposite membranes by a simple casting method. Investigating mechanical properties, thermal stability, and conductivity of the polyetherimide (PEI)/MWCNT composites showed a unique combination of properties, such as high electrical conductivity, high mechanical properties, and high thermal stability at a low content of 1.0 wt % loading of ODA modified MWCNTs. Moreover, electrical resistivity decreased around 10 orders of magnitude with only 0.5 wt % of modified MWCNTs.

We report the preparation and characterization of three pyrimidine-based monomers, specifically: 1-(2-diallylaminoethyl)uracil, 1-(2-diallylaminoethyl)thymine and 1-(2-diallylaminoethyl)cytosine. Monomer synthesis was initiated by reaction of the pyrimidine with ethylene carbonate to form the hydroxyethyl adduct which was subsequently chlorinated to afford the chloroethyl intermediate. Reaction of the chloroethyl derivatives with diallylamine resulted in the desired monomers. We demonstrated a two-fold increase in the overall yield of the three monomers in comparison to reported procedures. The cyclopolymerization and cyclo-copolymerization of 1-(2-diallylaminoethyl)pyrimidine trifluoroacetate salts in water resulted in low-yield homopolymers. In contrast, the neutral 1-(2-diallylaminoethyl)pyrimidines cyclo-copolymerized with sulfur dioxide and V-50 initiator to yield the corresponding copolymers in higher yields ranging from 30 to 60%.

Polydopamine-coated FeCo nanocubes (PDFCs) were successfully synthesized and tested under microwave irradiation of 2.45 GHz frequency and 0.86 W/cm² power. These particles were found to be non-toxic in the absence of irradiation, but gained significant toxicity upon irradiation. Interestingly, no increase in relative heating rate was observed when the PDFCs were irradiated in solution, eliminating nanoparticle (NP)-induced thermal ablation as the source of toxicity. Based on these studies, we propose that microwave-induced redox processes generate the observed toxicity.