This study provides the results of an experiment on the possibility of using high-volume ground granulated blast furnace slag (HVGGBFS)-based concrete as mass concrete. In addition to the control concrete, the total weight of the binder was 75% ground granulated blast furnace slag (GGBFS) and 25% ordinary Portland cement (OPC). For the aggregates, both natural and recycled aggregates were used. Three specimens with dimensions of 800 mm × 800 mm × 800 mm were prepared to simulate mass concrete. The workability, temperature aging and strength of the mass concrete were tested. The test results showed that utilizing HVGGBFS concrete as mass concrete can significantly reduce the heat of hydration due to the low heat of hydration of GGBFS, while the heat of hydration of GGBFS and recycled aggregate combination is 11.2% higher than normal concrete, with a slump that is 31.3% lower than that of plain concrete. The results also showed that the use of recycled aggregates in HVGGBFS concrete can significantly reduce workability. However, the compressive strength is higher than when natural aggregates are used due to the alkali activation effect caused by the recycled aggregates. The compressive strength at 7 and 28 days increased by 33.7% and 16.3%, respectively.

In order to conduct a comprehensive investigation into the effects of ground granulated blast furnace slag (GGBFS) on the dynamic mechanical properties and mesoscopic damage mechanisms of recycled aggregate concrete (RAC), a combined approach integrating material testing, microscopic characterization techniques, and theoretical analysis was adopted in this study. Two GGBFS replacement rates (0% and 35%) were considered. Uniaxial compression tests were performed to obtain data at different curing ages (T = 7 d, 28 d, 56 d, and 150 d) and strain rates ($\dot{\epsilon }$ = 10⁻⁵/s, 10⁻⁴/s, 10⁻³/s, and 10⁻²/s). The obtained data were complemented by nuclear magnetic resonance (NMR) and scanning electron microscopy (SEM) analyses to characterize the evolution of the microstructure and pore characteristics of the specimens. The findings demonstrated that prolonging the curing period continuously densified the microstructure of the specimens, resulting in a commensurate improvement in their initial macro-mechanical behavior. At curing ages exceeding 28 d, the secondary hydration reaction of GGBFS was found to generate additional C-S-H gel, which filled the internal microvoids within the specimens, reduced porosity, and further improved the initial macroscopic mechanical properties. Concurrently, the microstructural characteristics observed at different curing ages, in conjunction with the crack propagation and the fracture toughness effects associated with strain rate, further influenced the initiation, propagation patterns and paths of microcracks during uniaxial compression, as well as the adjustment of the effective stress framework. Furthermore, characteristic parameters describing the evolution of mesoscopic fracturing and yielding damage exhibited regular variations with curing age and strain rate. For specimens cured for 56 d, compared to those with a GGBFS replacement rate of 0%, specimens containing 35% GGBFS exhibited a 4.13% increase in peak stress and a 0.29% decrease in peak strain at $\dot{\epsilon }$ = 10⁻⁵/s. At a replacement rate of 35%, as the strain rate increased from $\dot{\epsilon }$ = 10⁻⁵/s to $\dot{\epsilon }$ = 10⁻²/s, the peak stress rose from −50.37 MPa to −60.74 MPa, whereas the peak strain dropped from −23.87 × 10⁻⁴ to −22.15 × 10⁻⁴. This study provides significant scientific evidence and a theoretical framework for the engineering application of GGBFS-modified RAC under varying strain rate conditions.