In order to promote the degradation of PLA in seawater, a series of seawater-degradable polyester blends PVA/PLA were prepared by blending biodegradable polylactic acid (PLA) with water-soluble modified polyvinyl alcohol (PVA) in this paper. ADR 4370S was introduced to bring a certain degree of improvement in compatibility of PVA/PLA blends. The results of degradation test in natural seawater for 180 days show that the weight loss of PVA/PLA blends in seawater is much higher compared with that of pure PLA. PVA can be used as an effective hydrolysis accelerator for PLA matrix, helping to significantly reduce the molecular weight of PLA. The channels caused by dissolution/swelling of PVA facilitate the entry of water and microorganisms into the materials to contact with PLA, thereby promoting the degradation process of PLA matrix itself. Thus, both dissolution/swelling of PVA and degradation of PLA occur in PVA/PLA blends, and the degree of rapid dissolution of PVA in the early stage determines the degree of degradation of PLA.

Biodegradable mulches (BDMs) are considered promising alternative green materials to achieve the substitution of polythene (PE) films to reduce plastic pollution. However, whether the BDMs are sufficiently effective to promote cotton production as PE film is a controversial topic. In this study, laboratory determination and field experiments were conducted with one pure Poly(butylene adipate-co-terephthalate) (PBAT) film (BDM), two commercial PBAT-based films (BDM1 and BDM2), and one PE film to (ⅰ) compare the degradation behavior, morphology, and property changes during field application, and (ⅱ) reveal their effects on biomass accumulation and cotton yield. Degradation behavior, degradation rate, structure, thermal stability, crystallinity, and molecular weight changes of the films before and after mulching were investigated and characterized. Water vapor transmission rate and mechanical properties of the films and the effects these on soil temperature, crop growth, and cotton yield were discussed. Results show that the three PBAT-based mulch films gradually degraded during mulching. The molecular weight, thermal stability, and crystallinity of BDM1 and BDM2 decreased. Interestingly, BDM showed the opposite characteristics, but the degradation degree was greatest at harvest. PE film showed no significant changes in its microscopic appearance, thermal performance, or properties. These PBAT-based films were positively correlated with the complete coverage period of the films. In-depth studies focused on BDMs with a longer mulching period must be developed to promote the substitution of BDMs into PE to reduce the residual mulch pollution in cotton fields.