This paper describes research focused on investigating the effect of hydrogen (H) atom insertion into the grain boundaries of polycrystalline diamond (PCD) films. This is required in order to understand the key morphological, chemical, physical, and electronic properties of the films. The PCD films were grown using the hot filament chemical vapor deposition (HFCVD) process, with flowing Ar gas mixed with CH₄ and H₂ gases to control film growth into microcrystalline diamond (MCD, 0.5–3 µm grain sizes), nanocrystalline diamond (NCD, 10–500 nm grain sizes), and ultrananocrystalline diamond (UNCD, 2–5 nm grain sizes) films depending on the Ar/CH₄/H₂ flow ratios. This study focused on measuring the H atom concentration of the PCD films to determine the effect on the properties indicated above. A simple model is presented, including a hypothesis that the two dangling bonds per unit cell of C atoms serve as the site of hydrogen incorporation. This correlates well with the observed concentration of H atoms in the films. Dangling bonds which are not passivated by hydrogen are postulated to form surface structures which include C double bonds. The Raman peak from these surface structures are the same as observed for transpolyacetyline (TPA). The data reveal that the concentration of H atoms at the grain boundaries is around 1.5 × 10¹⁵ atoms/cm² regardless of grain size. Electrical current measurements, using a conductive atomic force microscopy (CAFM) technique, were performed using an MCD film, showing that the current is concentrated at the grain boundaries. Ultraviolet photo electron spectroscopy (UPS) confirmed that all the PCD films exhibited a metallic behavior. This is to be expected if the nature of grain boundaries is the same regardless of grain size.

In situ and time-resolved infrared absorption spectroscopic measurements reveal that, under typical processing conditions ($\sim 300\text{K}$ , approximately Torr pressures), ${\text{XeF}}_2$ reacts efficiently but very differently with Mo and Si substrates. This kinetic study of the surface etching processes, based on the time evolution of both reactants and products, demonstrates that the mechanisms for Mo and Si etching are different. While ${\text{XeF}}_2$ produces substantial roughening and a thick fluorosilyl layer on the crystalline Si surface $\left(>200\text{nm}\right)$ , it only reacts with the surface atoms of amorphous Mo with substantially slower kinetics. The measured kinetics are quantified by simulation and the final profile experimentally obtained on etched Si surface is shown to be consistent with a recent theoretical study of the characteristic diffusion-controlled etching of silicon.

The biological response of multi-walled carbon nanotubes (MWNTs) is related to their physicochemical properties and a thorough MWNT characterization should accompany an assessment of their biological activity, including their potential toxicity. Beyond characterizing the physicochemical properties of MWNTs from different sources or manufacturers, it is also important to characterize different production lots of the same MWNT product from the same vendor (i.e., lot-to-lot batch consistency). Herein, we present a comprehensive physicochemical characterization of two lots of commercial pristine MWNTs (pMWNTs) and carboxylated MWNTs (cMWNTs) used to study the response of mammalian macrophages to MWNTs. There were many similarities between the physicochemical properties of the two lots of cMWNTs and neither significantly diminished the 24-h proliferation of RAW 264.7 macrophages up to the highest concentration tested (200 μg cMWNTs/mL). Conversely, several physicochemical properties of the two lots of pMWNTs were different; notably, the newer lot of pMWNTs displayed less oxidative stability, a higher defect density, and a smaller amount of surface oxygen species relative to the original lot. Furthermore, a 72-h half maximal inhibitory concentration (IC-50) of ~90 µg pMWNTs/mL was determined for RAW 264.7 cells with the new lot of pMWNTs. These results demonstrate that subtle physicochemical differences can lead to significantly dissimilar cellular responses, and that production-lot consistency must be considered when assessing the toxicity of MWNTs.