It has long been an aspirational goal to create artificial evaporators that allow omnidirectional energy absorptance, adequate water supply, and fast vapor transportation, replicating the feat of plant transpiration, to solve the global water crisis. This work reveals that magnolia fruits, as a kind of tree‐like living organism, can be outstanding 3D tree‐like evaporators through a simple carbonization process. The arterial pumping, branched diffusion, and confined evaporation are achieved by the “trunk,” “branches,” and “leaves,” respectively, of the mini tree. The mini tree possesses omnidirectional high light absorptance with minimized heat loss and gains energy from the environment. Water confined in the fruit possesses reduced vaporization enthalpy and transports quickly following the Murray's law. A record‐high vapor generation rate of 1.22 kg m⁻² h⁻¹ in dark and 3.15 kg m⁻² h⁻¹ under 1 sun illumination is achieved under the assistance of the gully‐like furry surface. The “absorption of nutrients” enables the fruit to recover valuable heavy metals as well as to produce clean water from wastewater efficiently. These findings not only reveal the hidden talent of magnolia fruits as cheap materials for vapor generation but also inspire future development of high‐performance, full‐time, and all‐weather vapor generation and water treatment devices.

With the ever-growing demands for larger size and high resolution displays, Micro-light-emitting diode (Micro-LED) display with quantum dots (QDs) film as color conversion layers (CCLs) has become one of the most promising candidates of future display for its advantages in low power consumption and wide color range. In this study, we report a novel full-color display based on blue Micro LED, which has patterned red and green QDs color conversion (QDCC) layers fabricated by inkjet printing (IJP). A structure of double-layer bank was designed to reduce color deviation, prevent crosstalk, and flatten the QDCC layer. By optimizing the thickness of the red/green QDCC layers and the wavelength of blue Micro LED backlights, a full-color QDCC-LED display with 228 PPI resolution and size of 1.11-inch was successfully fabricated and showed superb performance. We not only effectively reduced crosstalk, but also improved the color conversion efficiency of QDs. In addition, this QDCC-LED display prepared by embedded bonding process shows a color gamut of 107.53% NTSC. Graphical Abstract