Pervious concrete (PC), as an environmental friendly material, can be very important in solving urban problems and mitigating the impact of climate change; i.e., flooding, urban heat island phenomena, and groundwater decline. The objective of this research is to evaluate the strength, permeability, and freeze-thaw durability of PC with different aggregate sizes, porosities, and water-binder ratios. The orthogonal experiment method is employed in the study and nine experiments are conducted. The compressive strength, flexural strength, permeability coefficient, porosity, density, and freeze-thaw durability of PC mixtures are tested. Range analysis and variance analysis are carried out to analyze the collected data and estimate the influence of aggregate size, porosity, and water-binder ratio on PC properties. The results indicate that porosity is the most important factor determining the properties of PC. High porosity results in better permeability, but negatively affects the mechanical strength and freeze-thaw durability. PC of 15% porosity can obtain high compressive strength in excess of 20 MPa and favorable freeze-thaw durability of 80 cycles without sacrificing excessive permeability. Aggregate size also has a significant effect on freeze-thaw durability and mechanical strength. Small aggregate size is advantageous for PC properties. PC with 4.75–9.5 mm coarse aggregate presents excellent freeze-thaw durability. The influence of the water-binder ratio on PC properties is not as significant as that of aggregate size and porosity. An optimal mix ratio is required to trade-off between permeability, mechanical strength, and freeze-thaw durability.

Pervious concretes, as sustainable pavement materials, have great advantages in addressing a number of environmental issues. Fly ash, as the industrial by-product waste, is the most commonly used as cement substitute in concrete. The objective of this paper is to study the effects of waste fly ash on properties of pervious concrete. Fly ash was used to replace cement with equivalent volume method at different levels (3%, 6%, 9%, and 12%). The control pervious concrete and fly ash modified pervious concrete were prepared in the laboratory. The porosity, permeability, compressive strength, flexural strength, and freeze–thaw resistance of all mixtures were tested. The results indicated that the addition of fly ash decreased the early-age (28 d) compressive strength and flexural strength, but the long-term (150 d) compressive strength and flexural strength of fly ash modified pervious concrete were higher than that of the early-age. The adverse effect of fly ash on freeze–thaw resistance of pervious concrete was observed when the fly ash was added. The porosity and permeability of all pervious concrete mixtures changed little with the content of fly ash due to the use of equal volume replacement method. Although fly ash is not positive to the properties of pervious concrete, it is still feasible to apply fly ash as a substitute for cement in pervious concrete.

Pervious concretes, such as sustainable pavement materials, have great advantages in solving urban flooding, promoting urban ecological balance, and alleviating urban heat island effect, due to its special porous structure. However, pervious concrete typically has high porosity and low strength. The insufficient strength and poor freeze-thaw durability are important factors that restrict its wide application, especially in seasonal frozen areas. Improving the strength and freeze-thaw resistance of pervious concrete will expand its application. Silica fumes, as an industrial by-product waste and supplementary cementitious material, play an important role in improving concrete performance. The objective of this paper was to study the effects of silica fumes on properties of sustainable pervious concrete. Silica fumes were used to replace cement with the equivalent volume method at different levels (3%, 6%, 9%, and 12%). The control pervious concrete and silica fume-modified pervious concrete mixtures were prepared in the lab. The porosity, permeability, compressive strength, flexural strength, and freeze-thaw resistance properties of all mixtures were tested. The results indicated that the addition of silica fumes significantly improved the strength and freeze-thaw resistance of pervious concrete. The porosity and permeability of all pervious concrete mixtures changed little with the content of silica fumes due to the adoption of the equal volume replacement method.

Due to the negative effects that derive from large impervious surfaces in urban areas, pervious concrete has been developed, and has become an environmentally friendly pavement material. As a porous and permeable material, pervious concrete presents an overwhelming advantage in solving urban problems, such as flooding, groundwater decline, urban heat island phenomena, etc. Waste crumb rubber has been verified as a feasible modifier for pavement material. The objective of this paper is to explore the effects of rubber particle size and incorporation level on the permeability, mechanical properties, and freeze–thaw resistance of pervious concrete. Two kinds of rubbers (fine and coarse) with four incorporation levels (2%, 4%, 6%, and 8%) are used in the experiment. Permeability, compressive strength, flexural strength, flexural strain, and freeze–thaw resistance are tested. The results indicate that the addition of rubber slightly decreases strength and permeability, but significantly enhances ductility and freeze-thaw resistance. Fine crumb rubber with a suitable incorporation level could remarkably improve the ductility and freeze–thaw resistance of pervious concrete without sacrificing excessively strength and permeability.

The urban environment is facing serious problems caused by automobile exhaust pollution, which has led to a great impact on human health and climate, and aroused widespread concern of the government and the public. Nano titanium dioxide (TiO₂), as a photocatalyst, can be activated by ultraviolet irradiation and then form a strong REDOX potential on the surface of the nano TiO₂ particles. The REDOX potential can degrade the automobile exhaust, such as nitrogen oxides (NO_x) and hydrocarbons (HC). In this paper, a photocatalytic environmentally friendly pervious concrete (PEFPC) was manufactured by spraying nano TiO₂ on the surface of it and the photocatalytic performance of PEFPC was researched. The nano TiO₂ particle size, TiO₂ dosage, TiO₂ spraying amount, and dispersant dosage were selected as factors to investigate the efficiency of photocatalytic degradation of automobile exhaust by PEFPC. Moreover, the environmental scanning electron microscope (ESEM) was used to evaluate the distribution of nano TiO₂ on the surface of the pervious concrete, the distribution area of nano TiO₂ was obtained through Image-Pro Plus, and the area ratio of nano TiO₂ to the surface of the pervious concrete was calculated. The results showed that the recommended nano TiO₂ particle size is 25 nm. The optimum TiO₂ dosage was 10% and the optimum dispersant dosage was 5.0%. The photocatalytic performance of PEFPC was best when the TiO₂ spraying amount was 333.3 g/m². The change in the photocatalytic ratio of HC and NO_x is consistent with the distribution area of nano TiO₂ on the surface of the pervious concrete. In addition, the photocatalytic performance of PEFPC under two light sources (ultraviolet light and sunlight) was compared. The results indicated that both light sources were able to stimulate the photocatalytic performance of PEFPC. The research provided a reference for the evaluation of automobile exhaust removal performance of PEFPC.

Due to the superiorities of Styrene butadiene styrene (SBS) modified asphalt, it is widely used in civil engineering application. Meanwhile, accurately predicting and obtaining performance parameters of SBS modified asphalt in unison is difficult. At present, it is essential to discover an accurate and simple method between the input and output data. ANNs are used to model the performance and behavior of materials in place of conventional physical tests because of their adaptability and learning. The objective of this study discussed the application of ANNs in determining performance of SBS modified asphalt, based on attenuated total reflection Fourier transform infrared spectroscopy (ATR-FTIR) tests. A total of 150 asphalt mixtures were prepared from three matrix asphalt, two SBS modifiers and five modifier dosages. With the most suitable algorithm and number of neurons, an ANN model with seven hidden neurons was used to predict SBS content, needle penetration and softening point by using infrared spectral data of different modified asphalts as input. The results indicated that ANN-based models are valid for predicting the performance of SBS modified asphalt. The coefficient of determination (R²) of SBS content, softening point and penetration prediction models with the same grade of asphalt exceeded 99%, 98% and 96%, respectively. It can be concluded that ANNs can provide well-satisfied regression models between the SBS content and infrared spectrum statistics sets, and the precision of penetration and softening point model founded by the same grade of asphalt is high enough to can meet the forecast demand.