During the last years engineered nanoparticles (NPs) have been extensively used in different technologies and consequently many questions have arisen about the risk and the impact on human health following exposure to nanoparticles. Nevertheless, at present knowledge about the cytotoxicity induced by NPs is still largely incomplete. In this context, we have investigated the cytotoxicity induced by gold nanoparticles (AuNPs), which differed in size and purification grade (presence or absence of sodium citrate residues on the particle surface) in vitro, in the human alveolar type-II (ATII)-like cell lines A549 and NCIH441.

The use of gold nanoparticles (AuNPs) for diagnostic applications and for drug and gene-delivery is currently under intensive investigation. For such applications, biocompatibility and the absence of cytotoxicity of AuNPs is essential. Although generally considered as highly biocompatible, previous in vitro studies have shown that cytotoxicity of AuNPs in certain human epithelial cells was observed. In particular, the degree of purification of AuNPs (presence of sodium citrate residues on the particles) was shown to affect the proliferation and induce cytotoxicity in these cells. To expand these studies, we have examined if the effects are related to nanoparticle size (10, 11 nm, 25 nm), to the presence of sodium citrate on the particles' surface or they are due to a varying degree of internalization of the AuNPs. Since two cell types are present in the major barriers to the outside in the human body, we have also included endothelial cells from the vasculature and blood brain barrier.

Background: To date silica nanoparticles (SNPs) play an important role in modern technology and nanomedicine. SNPs are present in various materials (tyres, electrical and thermal insulation material, photovoltaic facilities). They are also used in products that are directly exposed to humans such as cosmetics or toothpaste. For that reason it is of great concern to evaluate the possible hazards of these engineered particles for human health. Attention should primarily be focussed on SNP effects on biological barriers. Accidentally released SNP could, for example, encounter the alveolar-capillary barrier by inhalation. In this study we examined the inflammatory and cytotoxic responses of monodisperse amorphous silica nanoparticles (aSNPs) of 30 nm in size on an in vitro coculture model mimicking the alveolar-capillary barrier and compared these to conventional monocultures. Methods: Thus, the epithelial cell line, H441, and the endothelial cell line, ISO-HAS-1, were used in monoculture and in coculture on opposite sides of a filter membrane. Cytotoxicity was evaluated by the MTS assay, detection of membrane integrity (LDH release), and TER (Transepithelial Electrical Resistance) measurement. Additionally, parameters of inflammation (sICAM-1, IL-6 and IL-8 release) and apoptosis markers were investigated. Results: Regarding toxic effects (viability, membrane integrity, TER) the coculture model was less sensitive to apical aSNP exposure than the conventional monocultures of the appropriate cells. On the other hand, the in vitro coculture model responded with the release of inflammatory markers in a much more sensitive fashion than the conventional monoculture. At concentrations that were 10-100fold less than the toxic concentrations the apically exposed coculture showed a release of IL-6 and IL-8 to the basolateral side. This may mimic the early inflammatory events that take place in the pulmonary alveoli after aSNP inhalation. Furthermore, a number of apoptosis markers belonging to the intrinsic pathway were upregulated in the coculture following aSNP treatment. Analysis of the individual markers indicated that the cells suffered from DNA damage, hypoxia and ER-stress. Conclusion: We present evidence that our in vitro coculture model of the alveolar-capillary barrier is clearly advantageous compared to conventional monocultures in evaluating the extent of damage caused by hazardous material encountering the principle biological barrier in the lower respiratory tract.

The repair and regeneration of large bone defects, including the formation of functional vasculature, represents a highly challenging task for tissue engineering and regenerative medicine. Recent studies have shown that vascularization and ossification can be stimulated by mild heat stress (MHS), which would offer the option to enhance the bone regeneration process by relatively simple means. However, the mechanisms of MHS-enhanced angiogenesis and osteogenesis, as well as potential risks for the treated cells are unclear. We have investigated the direct effect of MHS on angiogenesis and osteogenesis in a co-culture system of human outgrowth endothelial cells (OECs) and primary osteoblasts (pOBs), and assessed cytotoxic effects, as well as the levels of various heat shock proteins (HSPs) synthesized under these conditions. Enhanced formation of microvessel-like structures was observed in co-cultures exposed to MHS (41°C, 1 h), twice per week, over a time period of 7–14 days. As shown by real-time polymerase chain reaction (PCR), the expression of vascular endothelial growth factor (VEGF), angiopoietin-1 (Ang-1), angiopoietin-2 (Ang-2), and tumor necrosis factor-alpha was up-regulated in MHS-treated co-cultures 24 h post-treatment. At the protein level, significantly elevated VEGF and Ang-1 concentrations were observed in MHS-treated co-cultures and pOB mono-cultures compared with controls, indicating paracrine effects associated with MHS-induced angiogenesis. MHS-stimulated co-cultures and OEC mono-cultures released higher levels of Ang-2 than untreated cultures. On the other hand MHS treatment of co-cultures did not result in a clear effect regarding osteogenesis. Nevertheless, real-time PCR demonstrated that MHS increased the expression of mitogen-activated protein kinase, interleukin-6, and bone morphogenetic protein 2, known as HSP-related molecules in angiogenic and osteogenic regulation pathways. In agreement with these observations, the expression of some selected HSPs also increased at both the mRNA and protein levels in MHS-treated co-cultures.

Providing adequate vascularization is one of the main hurdles to the widespread clinical application of bone tissue engineering approaches. Due to their unique role in blood vessel formation, endothelial cells (EC) play a key role in the establishment of successful vascularization strategies. However, currently available polymeric materials do not generally support EC growth without coating with adhesive proteins. In this work we present argon plasma treatment as a suitable method to render the surface of a 3D starch-based scaffold compatible for ECs, this way obviating the need for protein pre-coating. To this end we studied the effect of plasma modification on surface properties, protein adsorption and ultimately on several aspects regarding EC behaviour. Characterization of surface properties revealed increased surface roughness and change in topography, while at the chemical level a higher oxygen content was demonstrated. The increased surface roughness of the material, together with the changed surface chemistry modulated protein adsorption as indicated by the different adsorption profile observed for vitronectin. In vitro studies showed that human umbilical vein ECs (HUVECs) seeded on plasma-modified scaffolds adhered, remained viable, proliferated, and maintained the typical cobblestone morphology, as observed for positive controls (scaffold pre-coated with adhesive proteins). Furthermore, genotypic expression of endothelial markers was maintained and neighbouring cells expressed PECAM-1 at the single-cell-level. These results indicate that Ar plasma modification is an effective methodology with potential to be incorporated in biomaterial strategies to promote the formation of vascularized engineered bone.