Non-edible cellulose-containing biomass is a promising and abundant feedstock for simple sugar production. This study presents the results of different cellulose-containing materials (CCM) hydrolysis experiments with P. verruculosum enzyme complexes in laboratory conditions. Among the non-pretreated substrates, only a few had a relatively high convertibility—soy bean husks (31%) and sugar beat pulp (20%)—while wheat straw, oat husks, sunflower peals, and corn stalks had a low convertibility of 3% to 12%. This indicates that a major part of CCM needs pretreatment. Steam-exploded (with Ca(OH)₂) soy bean and oat husks (76% and 58%), fine ball-milled aspen wood and nitric acid-pretreated aspen wood (62% and 78%), and steam-exploded (with sulfuric acid) corn stalks (55%) had a high convertibility. Woody biomass pretreated with pulp and paper mills also had a high convertibility (56–78%)—e.g., never dried kraft hardwood and softwood pulp (both bleached and unbleached). These results demonstrate that effective cellulose-containing material processing into simple sugars is possible. Simple sugars derived from CCM using P. verruculosum preparation are a promising feedstock for the microbiological production of biofuels (bioethanol and biobutanol), aminoacids, and organic acids (e.g., lactic acid for polylactic acid production).

Non-edible cellulosic biomass from perennial herbaceous plants is a promising and abundant feedstock for replacing slow-growing woody plants used in biotechnological applications. Herbaceous plant biomass, as other types of plant biomass, requires pretreatment before biochemical conversion. In this study, miscanthus straw was pretreated using different methods and subjected to enzymatic hydrolysis with Penicillium verruculosum enzyme complexes under laboratory conditions. The convertibility after enzymatic hydrolysis varied from 15% to 66%, depending on the pretreatment method. Dilute alkaline pretreatment showed the highest convertibility compared to other methods, reaching up to 66%. The efficiency of dilute acid pretreatment was relatively low compared to other methods. The maximum convertibility was 37% for sulfuric acid pretreatment (the least efficient) and 51% for nitric acid. Convertibility was almost equal with 43% for white liquor and 46% for hot water. The glucose-to-xylose ratio was 4.7:1 for dilute alkaline pretreatment and 11–13:1 for white liquor. Both sulfuric and nitric acid resulted in a low xylose content in the enzymatic hydrolysates. Low-xylose hydrolysates with less than 2% of the glucose amount can be produced by hot water pretreatment. Preparation C, enriched with endoglucanase I from T. reesei and endoglucanase II from P. verruculosum, was found to be the most effective of the different enzyme preparations (EPs) tested.

This study examines the nature of enzymatic degradation of polyethylene terephthalate (PET) films mediated by a novel recombinant LCC^ICCG PETase enzyme preparation based on P. verruculosum fungus. The investigation was conducted using amorphous PET samples and PET samples with varying degrees of crystallinity as substrates for PETase-catalyzed hydrolysis under different temperature and pH conditions. Mechanical testing revealed that enzymatic treatment reduced the yield stress by 20–25%, tensile strength by approximately twofold, and elongation at break by 5–10 times, while the deformation mechanism remained unchanged. Enzymatic degradation under acidic conditions was ineffective, whereas increasing the pH to 9–10 markedly accelerated PET degradation and the associated deterioration of mechanical properties. Thermal analysis (TGA, DSC) and microscopy (optical and scanning electron microscopy) demonstrated that degradation was localized at the polymer surface, leading to the formation of cavities, cracks, and submicron-sized pores rather than bulk material disintegration. An inverse correlation was observed between PET crystallinity and susceptibility to enzymatic degradation: samples with crystallinity below 13% could be almost completely degraded, whereas samples with crystallinity above 30% exhibited little or no measurable weight loss over the same period. Low-crystallinity PET underwent rapid degradation accompanied by a transient increase in crystallinity, while highly crystalline PET primarily accumulated surface defects that nevertheless caused a substantial loss of mechanical strength. Consequently, the experimental data obtained in this study provide useful information for understanding PET degradation and for future studies on enzymatic PET recycling. The systematization of feedstock characteristics and the elucidated patterns of enzymatic degradation will enable optimization of pretreatment, enzymatic hydrolysis, and monomer recovery process parameters, thereby facilitating the eventual production of secondary raw materials.