The trap parameters of defects in Si/CaF2 multilayered structures were determined from the analysis of optical charging spectroscopy measurements. Two kinds of maxima were observed. Some of them were rather broad, corresponding to “normal” traps, while the others, very sharp, were attributed to stress-induced traps. A procedure of optimal linear smoothing the noisy experimental data has been developed and applied. This procedure is based on finding the minimal value of the relative error with respect to the value of the smoothing window. In order to obtain a better accuracy for the description of the trapping-detrapping process, a Gaussian temperature dependence of the capture cross-sections characterizing the stress-induced traps was introduced. Both the normal and the stress-induced traps have been characterized, including some previously considered as only noise features.

Films of SiGe nanocrystals (NCs) in oxide have the advantage of tuning the energy band gap by adjusting SiGe NCs composition and size. In this study, SiGe-SiO₂ amorphous films were deposited by magnetron sputtering on Si substrate followed by rapid thermal annealing at 700, 800 and 1000 °C. We investigated films with Si:Ge:SiO₂ compositions of 25:25:50 vol.% and 5:45:50 vol.%. TEM investigations reveal the major changes in films morphology (SiGe NCs with different sizes and densities) produced by Si:Ge ratio and annealing temperature. XPS also show that the film depth profile of SiGe content is dependent on the annealing temperature. These changes strongly influence electrical and photoconduction properties. Depending on annealing temperature and Si:Ge ratio, photocurrents can be 10³ times higher than dark currents. The photocurrent cutoff wavelength obtained on samples with 25:25 vol% SiGe ratio decreases with annealing temperature increase from 1260 nm in SWIR for 700 °C annealed films to 1210 nm for those at 1000 °C. By increasing Ge content in SiGe (5:45 vol%) the cutoff wavelength significantly shifts to 1345 nm (800 °C annealing). By performing measurements at 100 K, the cutoff wavelength extends in SWIR to 1630 nm having high photoresponsivity of 9.35 AW⁻¹.

In this work we prepared films of amorphous germanium nanoparticles embedded in SiO₂ deposited by magnetron sputtering on Si and quartz heated substrates at 300, 400 and 500 °C. Structure, morphology, optical, electrical and photoconduction properties of all films were investigated. The Ge concentration in the depth of the films is strongly dependent on the deposition temperature. In the films deposited at 300 °C, the Ge content is constant in the depth, while films deposited at 500 °C show a significant decrease of Ge content from interface of the film with substrate towards the film free surface. From the absorption curves we obtained the Ge band gap of 1.39 eV for 300 °C deposited films and 1.44 eV for the films deposited at 500 °C. The photocurrents are higher with more than one order of magnitude than the dark ones. The photocurrent spectra present different cutoff wavelengths depending on the deposition temperature, i.e. 1325 nm for 300 °C and 1267 nm for 500 °C. These films present good responsivities of 2.42 AW⁻¹ (52 μW incident power) at 300 °C and 0.69 AW⁻¹ (57 mW) at 500 °C and high internal quantum efficiency of ∼445% for 300 °C and ∼118% for 500 °C.

The influence of the shape of silicon quantum dots embedded in an amorphous silica matrix on the quantum confinement energy levels, as well as that of the $\text{Si}/{\text{SiO}}_2$ potential barrier, are studied. The energy levels are computed using both the infinite and finite rectangular quantum well models for spherical quantum dots and the infinite rectangular quantum well for prolate spheroidal quantum dots. The results are compared with each other and also with the experimental activation energies obtained from the temperature dependence of the dark current. These activation energies are identified with the differences between the quantum confinement energies, subject to the selection rules. The finite rectangular quantum well model takes into account the experimental value of the finite potential barrier and the matrix-to-dot electron mass ratio. The energy levels are smaller than those for the infinite rectangular quantum well case; they decrease when the potential barrier decreases and the mass ratio increases. Different aspects of the models are discussed. All the errors are less than about 4%. The spheroidal shape lifts the degeneracy on the magnetic quantum number. The energy levels can decrease or increase with eccentricity as a consequence of the different quantum confinement effects along the major and minor axes. The supplementary information on the magnetic quantum number is beneficial for optical applications.