Young’s modulus (E) is one of the most important parameters in the mechanical properties of solid materials. Young’s modulus is proportional to the stress and strain values. There are several experimental and theoretical methods for gaining Young’s modulus values, such as stress–strain curves in compression and tensile tests, electromagnetic-acoustic resonance, ultrasonic pulse echo and density functional theory (DFT) in different basis sets. Apparently, preparing specimens for measuring Young’s modulus through the experimental methods is not convenient and it is time-consuming. In addition, for calculating Young’s modulus values by software, presumptions of data and structures are needed. Therefore, this new method for gaining the Young’s modulus values of crystalline materials is presented. Herein, the new method for calculating Young’s modulus of crystalline materials is extracted by X-ray diffraction. In this study, Young’s modulus values were gained through the arbitrary planes such as random (hkl) in the research. In this study, calculation of Young’s modulus through the relationship between elastic compliances, geometry of the crystal lattice and the planar density of each plane is obtained by X-ray diffraction. Sodium chloride (NaCl) with crystal lattices of FCC was selected as the example. The X-ray diffraction, elastic stiffness constant and elastic compliances values have been chosen by the X’Pert software, literature and experimental measurements, respectively. The elastic stiffness constant and Young’s modulus of NaCl were measured by the ultrasonic technique and, finally, the results were in good agreement with the new method of this study. The aim of the modified Williamson–Hall (W–H) method in the uniform stress deformation model (USDM) utilized in this paper is to provide a new approach of using the W–H equation, so that a least squares technique can be applied to minimize the sources of errors.

Taking into account X-ray diffraction, one of the well-known methods for calculating the stress-strain of crystals is Williamson-Hall (W–H). The W-H method has three models, namely (1) Uniform deformation model (UDM); (2) Uniform stress deformation model (USDM); and (3) Uniform deformation energy density model (UDEDM). The USDM and UDEDM models are directly related to the modulus of elasticity (E). Young’s modulus is a key parameter in engineering design and materials development. Young’s modulus is considered in USDM and UDEDM models, but in all previous studies, researchers used the average values of Young’s modulus or they calculated Young’s modulus only for a sharp peak of an XRD pattern or they extracted Young’s modulus from the literature. Therefore, these values are not representative of all peaks derived from X-ray diffraction; as a result, these values are not estimated with high accuracy. Nevertheless, in the current study, the W-H method is used considering the all diffracted planes of the unit cell and super cells (2 × 2 × 2) of Hydroxyapatite (HA), and a new method with the high accuracy of the W-H method in the USDM model is presented to calculate stress (σ) and strain (ε). The accounting for the planar density of atoms is the novelty of this work. Furthermore, the ultrasonic pulse-echo test is performed for the validation of the novelty assumptions.

Calcium titanate-CaTiO₃ (perovskite) has been used in various industrial applications due to its dopant/doping mechanisms. Manipulation of defective grain boundaries in the structure of perovskite is essential to maximize mechanical properties and stability; therefore, the structure of perovskite has attracted attention, because without fully understanding the perovskite structure and diffracted planes, dopant/doping mechanisms cannot be understood. In this study, the areas and locations of atoms and diffracted planes were designed and investigated. In this research, the relationship between Young’s modulus and planar density of unit cell, super cells (2 × 2 × 2) and symmetry cells of nano CaTiO₃ is investigated. Elastic constant, elastic compliance and Young’s modulus value were recorded with the ultrasonic pulse-echo technique. The results were C₁₁ = 330.89 GPa, C₁₂ = 93.03 GPa, C₄₄ = 94.91 GPa and E = 153.87 GPa respectively. Young’s modulus values of CaTiO₃ extracted by planar density were calculated 162.62 GPa, 151.71 GPa and 152.21 GPa for unit cell, super cells (2 × 2 × 2) and symmetry cells, respectively. Young’s modulus value extracted by planar density of symmetry cells was in good agreement with Young’s modulus value measured via ultrasonic pulse-echo.

In this work, TiO2 and TiO2-SiO2 thin films on glass substrates were prepared by the sol-gel dip coating process. X-ray diffraction (XRD), Fourier transfor