The results of an experimental program on shear-strengthening of flat slabs using Glass Fiber Reinforced Polymer (GFRP) rods are presented. A total of seven specimens were tested under an upward concentric monotonic loading until failure. One specimen served as a control and was tested without any modification. The remaining six specimens were strengthened with post-installed GFRP rods in single (SG), double (DB), and radial (RD) patterns within shear critical parameters around the centric column. The results of this experimental study suggest that GFRP rods are capable of enhancing both the peak load and deformation capacity. Furthermore, brittle failure associated with punching shear failure was successfully avoided by all strengthening patterns. Of all of the patterns, the RD pattern resulted in maximum peak load increase and corresponding deformation capacity while the lowest bound was created by the SG pattern. The results suggested that SG, DB and RD patterns enhanced ultimate loads up to 9.1, 11.3 and 15.7% while corresponding deflections increased up to 109, 136 and 154%. Strain measurement on flexural reinforcement suggested that all strengthened specimens were able to withstand higher longitudinal strains than yield. It was further shown that reducing the spacing between the GFRP rods efficiently enhanced peak loads, nevertheless, neither this change was proportional, nor did it result in an enhanced energy dissipation capacity. In the end, recommendations of American Concrete Institute (ACI) for the shear strength of two-way systems were modified to incorporate the contributions from GFRP rods. The results indicate that the proposed analytical approach provides an excellent match with the experimental results.

Salient features of lightweight aggregate concrete (LAC) include noticeable fire resistance, high strength-to-weight ratio, and low magnitude of dead loads. Further, LAC has a low cost, eases construction practices, and possesses an environment-friendly nature. On the downside, LAC has substandard mechanical properties in comparison to normal aggregate concrete. Natural fiber-reinforced polymers (FRPs) have shown their potential in ameliorating the mechanical properties of natural aggregate concrete. So far, no study has been conducted to assess the efficacy of hemp rope confinement to strengthen lightweight aggregate concrete especially comprising rectilinear sections. This study aimed to overcome the substandard nature of LAC. A low-cost, sustainable, and environmentally green solution in the form of natural hemp rope layers is proposed. Twenty-four square concrete specimens were tested in three groups depending upon the presence and quantity of lightweight aggregates. It was found that concrete constructed with lightweight aggregates demonstrated lower ultimate compressive strength and strain as compared to normal aggregate concrete. Hemp rope-confined LAC showed enhanced ultimate compressive strength and strain. This enhancement was found to increase with the number of hemp rope layers. Several existing ultimate stress models were assessed to predict the ultimate compressive strength of the hemp rope-confined specimens. Only a single model was able to predict the ultimate compressive strength of the hemp rope-confined specimens with reasonable accuracy.

Experimental evidence have proved that punching shear capacity of flat slabs deteriorate with the presence of openings located within the critical perimeter around columns. It is understood that this deterioration varies inversely with the distance of openings from column’s face. However, effect of the shape of openings on punching shear capacity is not well known. This study presents experimental results of 14 flat specimens to investigate the effects of the number (2 and 4), shape (circular, square, and rectangular), and location (1 and 4 times of slab’s thickness from column’s face) of openings on punching shear strength. It was found that circular openings had least influence on punching capacity followed by square and rectangular openings, respectively. Further, placing openings at a distance of four times the slab’s thickness from column’s face had minimal impact on punching capacity. Further, increasing the number of openings from 2 to 4 substantially reduced the punching capacity. An effort was made to predict the punching capacities of all specimens using the descriptive equations of ACI 318-19 and Eurocode 2. Mean of the ratio of experimental to analytical results and standard deviation of ACI equations were found to be more accurate than those of Eurocode 2 predictions.