Equiatomic FeCo alloys with average particle size of 24 μm were sintered using spark plasma sintering (SPS) system at sintering temperatures of 1100, 800, and 850 °C for heating rates 50, 100, 300 °C/min by applying pressure of 50 MPa instantly at room temperature for sintering time of 5 and 15 minutes. The highest saturation induction was achieved at SPS conditions of 50 MPa, 50 °C/min, 1100 °C, without dwelling, of value 2.39 T. The saturation induction was improved with extending sintering time, the coercivity was higher in samples sintered at a fast heating rate in comparison to the slowest heating rate.