Poultry feathers make up for as much as 8.5% of chicken weight and represent a considerable amount of almost pure keratin waste which is not being adequately utilized at the present time. The present study dealt with the processing of poultry feathers through a two-stage alkaline-enzymatic hydrolysis. In the first stage, feathers were mixed with a 0.1 or 0.3% KOH water solution in a 1 : 50 ratio and were incubated at 70°C for 24 h. After adjusting pH to 9, the effects examined in the second processing stage on the amount of degraded feathers were those of proteolytic enzyme additions (1-5%), time (4-8 h) and temperature (50-70°C). Processing feathers in 0.3% KOH and hydrolysing for 8 h in the second stage at 70°C with a 5% dose of enzyme (relative to dry feathers weight) produced approx. 91% degradation. Keratin hydrolysate is distinct for its high nitrogen content and reasonable inorganic solids level. Two-stage technology of alkaline-enzymatic hydrolysing of poultry feathers in an environment of 0.3% KOH achieves high efficiency under quite mild reaction conditions (temperature not exceeding 70°C with pH in a mildly alkaline region), and is feasible from an economic viewpoint. Keratin hydrolysate can find particular application in packaging technology (films, foils and encapsulates).

The effect of ionic surfactants and manufacturing methods on the separation and distribution of multi-wall carbon nanotubes (CNTs) in a silicone matrix are investigated. The CNTs are dispersed in an aqueous solution of the anionic surfactant dodecylbenzene sulfonic acid (DBSA), the cationic surfactant cetyltrimethylammonium bromide (CTAB), and in a DBSA/CTAB surfactant mixture. Four types of CNT-based composites of various concentrations from 0 to 6 vol.% are prepared by simple mechanical mixing and sonication. The morphology, electrical and thermal conductivity of the CNT-based composites are analyzed. The incorporation of both neat and modified CNTs leads to an increase in electrical and thermal conductivity. The dependence of DC conductivity versus CNT concentration shows percolation behaviour with a percolation threshold of about 2 vol.% in composites with neat CNT. The modification of CNTs by DBSA increases the percolation threshold to 4 vol.% due to the isolation/separation of individual CNTs. This, in turn, results in a significant decrease in the complex permittivity of CNT–DBSA-based composites. In contrast to the percolation behaviour of DC conductivity, the concentration dependence of thermal conductivity exhibits a linear dependence, the thermal conductivity of composites with modified CNTs being lower than that of composites with neat CNTs. All these results provide evidence that the modification of CNTs by DBSA followed by sonication allows one to produce composites with high homogeneity.

A sensor was made of a polymer composite composed of electrically-conductive carbon nanotubes embedded in elastic polyurethane. The composite was prepared using a polyurethane filter membrane, enmeshing it, and melding together with carbon nanotubes. Testing has shown that the composite can be elongated as much as 400% during which the electrical resistance is increased 270 times. The composite is also sensitive to compression and to organic solvent vapors. These properties indicate the composite could have applications as a highly-deformable strain and chemical vapors sensing element and also as flexible electromagnetic shielding or protection against lightning. As an example of the use of the composite as a strain sensor, the pressure variation between a shoe and floor during walking and knee flexion during cycling has been monitored.