Repair and regeneration of large bone defects is still a challenge, especially for defects which are the irregular and complex. Three-dimension (3D) printing, as an advanced fabrication technology, has been received considerable attentions due to its high precision, customized geometry and personalization. In this study, 3D porous polylactic acid/nano hydroxyapatite (PLA/nHA) composite scaffolds with enhanced osteogenesis and osteoconductivity were successfully fabricated by desktop fused deposition modeling technology. Morphological, composition and structural analysis revealed that nHA was successfully introduced into the PLA system and homogeneously dispersed in the printed PLA/nHA scaffolds. In vitro antibacterial experiment confirmed that the printed porous PLA/nHA scaffolds have good ability for loading and releasing vancomycin and levofloxacin. Meanwhile, MG-63 cells were used to evaluate the cytocompatibility of printed porous PLA/nHA scaffolds by proliferation and cellular morphological analysis. In addition, rabbit model was established to evaluate the osteogenesis and osteoconductivity of printed PLA/nHA scaffolds. All these results suggested that the 3D printed PLA/nHA scaffolds have great potential for repairing and regeneration of large bone defects.

Highly crystalline carbonated hydroxyapatite (CHA) nanorods with different carbonate contents were synthesized by a novel hydrothermal method. The crystallinity and chemical structure of synthesized nanorods were studied by Fourier transform infrared spectroscopy (FTIR), X-ray photo-electronic spectroscopy (XPS), X-ray diffraction (XRD), Raman spectroscopy, and transmission electron microscopy (TEM). The biocompatibility of synthesized CHA nanorods was evaluated by cell viability and alkaline phosphatase (ALP) activity of MG-63 cell line. The biocompatibility evaluation results show that these CHA nanorods are biologically active apatites and potentially promising bone-substitute biomaterials for orthopedic application.

For the first time we observed well-resolved Ca(I) and Ca(II) signal changes in fluorohydroxyapatites with different fluorine contents by solid state NMR. The experiment results show that fluorine ions perturb the chemical environment of Ca(II) ions and OH⁻ ions more than phosphorus tetrahedra and Ca(I) ions.