The nanostructure of poly(acrylic acid) (PAA) adsorption layer on the surface of mesoporous-activated carbon HPA obtained by physical activation of residue after supercritical extraction of hops was characterized. This characterization has been done based on the analysis of determination of adsorbed polymer amount, surface charge density, and zeta potential of solid particles (without and in the PAA presence). The SEM, thermogravimetric, FTIR, and MS techniques have allowed one to examine the solid surface morphology and specify different kinds of HPA surface groups. The effects of solution pH, as well as polymer molecular weight and concentration, were studied. The obtained results indicated that the highest adsorption on the activated carbon surface was exhibited by PAA with lower molecular weight (i.e., 2000 Da) at pH 3. Under such conditions, polymeric adsorption layer is composed of nanosized PAA coils (slightly negatively charged) which are densely packed on the positive surface of HPA. Additionally, the adsorption of polymeric macromolecules into solid pores is possible.

The aim of this study was to obtain a series of activated carbon samples by the chemical activation of low-rank coal. The precursor was impregnated with a NaOH solution. Activated carbons were characterized by determining their textural parameters and content of surface oxygen functional groups and by using an elemental analysis. The carbons were tested as potential adsorbents for the removal of liquid pollutants represented by rhodamine B. The effectiveness of rhodamine B removal from water solutions depended on the initial concentration of the dye, the mass of rhodamine B, and the pH and temperature of the reaction. The isotherm examination followed the Langmuir isotherm model. The maximum adsorption capacity of the rhodamine B was 119 mg/g. The kinetic investigation favored the pseudo-second-order model, indicating a chemisorption mechanism. The thermodynamic assessment indicated spontaneous and endothermic adsorption, with decreased randomness at the solid–liquid interface. The experiment revealed that a 0.1 M HCl solution was the most effective regenerative agent.

Activated carbons were obtained by physical and chemical activation of the residue of supercritical extraction of green tea leaves. All the adsorbents obtained were characterized by: elemental analysis, low-temperature nitrogen adsorption, and the contents of acidic and basic oxygen functional groups on the surface of activated carbons by the Boehm method. The activated carbons were micro- or micro-mesoporous with well-developed surface area ranging from 520 to 1085 m²/g and total pore volume from 0.62 to 0.64 cm³/g. The physical activation of the precursor led to the strongly basic character of the surface. Chemical activation with 50% solution of H₃PO₄ of the residue of supercritical extraction of green tea leaves promoted the generation of acidic functional groups. All adsorbents were used for methylene blue and methyl red adsorption from the liquid phase. The influence of the activation method, pH of the dye solution, contact time of adsorbent with adsorbate, the temperature of adsorption, and rate of sample agitation on the effectiveness of organic dyes removal was evaluated and optimized. In the process of methylene blue adsorption on adsorbents, an increase in the sorption capacity was observed with increasing pH of the adsorbate, while in the process of methyl red adsorption, the relation was quite the reverse. The adsorption data were analyzed assuming the Langmuir or Freundlich isotherm models. The Langmuir model better described the experimental results, and the maximum sorption capacity calculated for this model varied from 144.93 to 250.00 mg/g. The results of the kinetic analysis showed that the adsorption of organic dyes on activated carbon was following the pseudo-second-order model. The negative values of the Gibbs free energy indicate the spontaneous character of the process.