In this work, cellulose nanocrystals (CNCs) obtained by the acid hydrolysis of waste bamboo powder were used to synthesize cellulose nanocrystal-g-poly(acrylic acid-co-acrylamide) (CNC-g-P(AA/AM)) aerogels via graft copolymerization followed by freeze-drying. The structure and morphology of the resulting aerogels were characterized by Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM), and the CNC-g-P(AA/AM) aerogels exhibited excellent absorbent properties and adsorption capacities. Subsequent Pb(II) adsorption studies showed that the kinetic data followed the pseudo-second-order equation, while the adsorption isotherms were best described using the Langmuir model. The maximum Pb(II) adsorption capacity calculated by the Langmuir model reached up to 366.3 mg/g, which is a capacity that outperformed that of the pure CNC aerogel. The CNC-g-P (AA/AM) aerogels become structurally stable through chemical cross-linking, which enabled them to be easily regenerated in HCl solution and retain the adsorption capacity after repeated use. The aerogels were found to maintain 81.3% removal efficiency after five consecutive adsorption–desorption cycles. Therefore, this study demonstrated an effective method for the fabrication of an aerogel adsorbent with an excellent reusability in the effective removal of Pb(II) from aqueous solutions.

In this study, we reported PVA nanocomposite films enhanced by polyethyleneimine (PEI)-lignin contained cellulose nanofibers (LCNFs) via the solvent casting method. An easy and available method was preformed to prepare LCNFs using a supermasscolloider from unbleached bamboo waste after a mild alkaline pretreatment. The results demonstrate that LCNF–PEI can greatly improve mechanical, hydrophobic, anti-UV shielding and antibacterial properties of the composite films. The tensile strength of LPP1 film was improved to 54.56 MPa, which was higher than 39.37 MPa of PVA film. The water contact angle of films increased from 35° to 104° with an increase in LCNF content from 0 to 6 wt%. Meanwhile, the nanocomposite film demonstrated the effect of full shielding against ultraviolet light when the amount of LCNF–PEI reached 6 wt%. The addition of LCNF–PEI endowed excellent antibacterial activity (against S. aureus and E. coli), which indicated potential applications in the packaging field.

Lignin is an ideal substance for preparation of functional materials. Specifically, lignin nanospheres (LNPs) are formed by self-assembly of lignin molecules and show great application prospects in drug delivery, electrochemistry, catalysis, etc. At present, most superhydrophobic surfaces are mainly built using non-degradable inorganic particles and are still beset by defects such as poor environmental performance, easy aging, and low mechanical strength. In this study, an aqueous mixture containing LNPs, cellulose nanocrystals (CNCs) and polyvinyl alcohol (PVA) was sprayed onto wood surfaces and then modified by 1H,1H,2H,2H-perfluorooctyltrichlorosilane (FOTS) to obtain a superhydrophobic surface. In the superhydrophobic surface, LNPs were used as the main structural materials instead of inorganic particles, CNC was used as a reinforcement material and PVA was used as an adhesive. The resulting superhydrophobic surface showed a water contact angle (WCA) of 162°, good robustness resistance and long UV resistance in which the superhydrophobicity was still retained after exposure to ultra-high UV light (power of 1000 W) for 7 h, providing more directions for high-value application of lignin.

Complex preparation methods and weak mechanical properties of superhydrophobic coatings hinder their applicability. To address these problems, cellulose nanofibers (CNFs) were used as structural materials to augment the roughness properties, while polydimethylsiloxane (PDMS) was used as the adhesive. Based on the results of previous studies, superhydrophobic coatings with good mechanical properties can be prepared by spraying the mixture onto a substrate surface; herein, the mixture comprised modified CNFs and PDMS. The resulting coating possessed excellent superhydrophobicity, which allowed a maximum water contact angle (WCA) of 158°. Furthermore, it exhibited great knife-scratch-resistance properties and good abrasion performance, which was evaluated by abrading with 800-grit sandpaper for 19 cycles (abrasion length of 380 cm) under a 100 g load. Based on the simple operation and abrasion resistance, the coating shows great potential for practical application.

It is a challenge for a superhydrophobic coating to overcome the poor robustness and the rough surface structure that is usually built using inorganic particles that are difficult to degrade. In this study, a robust superhydrophobic coating is facilely prepared by using commercial biodegradable lignin-coated cellulose nanocrystal (L-CNC) particles after hydrophobic modification to build rough surface structures, and by choosing two different adhesives (double-sided tape and quick-setting epoxy) to support adhesion between the L-CNC particles and the substrates. In addition to excellent self-cleaning and water repellence properties, the resulting coatings show outstanding mechanical strength and durability against sandpaper abrasion, finger-wipe, knife-scratch, water jet, UV radiation, high temperature, and acidic and alkali solutions, possessing a wide application prospect.