Titanium carbide/reduced graphene oxide (Ti₃C₂T_z/rGO) gels were prepared by a one-step hydrothermal process.

Despite numerous prior reports of molten salt etching of MAX phases, few of these reports achieved water-dispersible MXene nanosheets, and none for Nb-based MXenes. Here we demonstrate the synthesis and aqueous dispersibility of Nb₂CT_Z nanosheets via molten salt etching and utilizing a KOH wash to add hydroxyl surface groups. However, little is known about the oxidation of molten salt etched MXenes compared to acid-etched MXenes. Our results indicate slower oxidation behavior for MXenes etched by molten salts, which may be due to the decreased amount of oxygen-containing terminal groups.

Intercalation in two-dimensional (2D) materials can modify their physical, chemical, and electronic properties. This modification enables the tailoring of 2D material characteristics, enhancing their performance and expanding their applications in various fields. The friction performance of 2D materials such as MoS₂ and graphite has a strong dependence on their interlayer spacing, and they exhibit an increase in d-spacing associated with a reduction in friction performance. The ability to control the interlayer spacing of Ti₃C₂T_z MXene has proven beneficial for energy storage applications such as batteries and supercapacitors, but no one has utilized this control of interlayer spacing for lubrication. In this study, we demonstrate that interlayer spacing of multilayer (ML) Ti₃C₂T_z MXene can be controlled through chemical intercalation and its direct effects on the electrical conductivity and friction performance. We observed a notable decrease in electrical conductivity in vacuum-filtered ML-Ti₃C₂T_z MXene films, which was attributed to an increased internal resistance resulting from the expansion of the interlayer gap. We also found a significant reduction in the coefficient of friction for ML-Ti₃C₂T_z MXene with an increased d-spacing. This reduction is attributed to a weakened attraction of individual ML-Ti₃C₂T_z MXene layers (intercalated). Under a tangential force, it becomes easier to slide within the larger interlayer gap with weakened van der Waals forces. This work provides insights into the tunability of MXene properties through interlayer spacing, offering potential applications requiring materials with specific electrical and friction characteristics.

Microplastics (MPs) are common environmental pollutants; however, little is known about their effects after ingestion by insects. Here we fed Aedes (Stegomyia) aegypti (L.) and Aedes (Stegomyia) albopictus (Skuse) mosquito larvae 1 µm polystyrene MPs and examined the impacts of ingestion on adult emergence rates, gut damage, and fungal and bacterial microbiota. Results show that MPs accumulate in the larval guts, resulting in gut damage. However, little impact on adult emergence rates was observed. MPs are also found in adult guts postemergence from the pupal stage, and adults expel MPs in their frass after obtaining sugar meals. Moreover, MPs effects on insect microbiomes need to be better defined. To address this knowledge gap, we investigated the relationship between MP ingestion and the microbial communities in Ae. albopictus and Ae. aegypti. The microbiota composition was altered by the ingestion of increasing concentrations of MPs. Amplicon sequence variants (ASVs) that contributed to differences in the bacterial and fungal microbiota composition between MP treatments were from the genera Elizabethkingia and Aspergillus, respectively. Furthermore, a decrease in the alpha diversity of the fungal and bacterial microbiota was observed in treatments where larvae ingested MPs. These results highlight the potential for the bacterial and fungal constituents in the mosquito microbiome to respond differently to the ingestion of MPs. Based on our findings and the effects of MP ingestion on the mosquito host micro- and mycobiome, MP pollution could impact the vector competence of important mosquito-transmitted viruses and parasites that cause human and animal diseases.