The industrial production of products, such as foil and aluminium alloy strips, begins with the production of semi-finished products in the form of slabs. These are produced by the continuous casting process, which is quick and does not allow the equilibrium conditions of solidification. Non-homogeneity—such as micro and macro segregation, non-equilibrium phases and microstructural constituents, as well as stresses arising during non-equilibrium solidification—are eliminated by means of homogenization annealing. In this way, a number of technological difficulties in the further processing of semi-finished products can be avoided. The aim of this research was the optimization of the homogenization annealing of the EN AW 8006 alloy. With the Thermo-Calc software, a thermodynamic simulation of equilibrium and non-equilibrium solidification was performed. Differential scanning calorimetry (DSC) was performed on selected samples in as-cast state and after various regimes of homogenization annealing and was used for the simulation of homogenization annealing. Using an optical microscope (OM), a scanning electron microscope (SEM) and an energy dispersion spectrometer (EDS), the microstructure of the samples was examined. Based on the results, it was concluded that homogenization annealing has already taken place after 8 h at 580 °C to the extent, that the material is then suitable for further processing.

In the present work, free-cutting aluminum alloy AA6026 with 1.1 wt.% bismuth addition was fabricated by different melt preparation methods in order to investigate whether the melt preparation route affects the solidification sequence and thus has an influence on the machinability of the alloy. All experiments were designed to simulate variable industrial conditions: addition of bismuth in an induction melting furnace, addition of bismuth in an electric resistance holding furnace, addition of bismuth together with grain refiner, effect of holding time and melt temperature before casting. Detailed thermodynamic analyses (DSC, Thermo-Calc) and microstructural characterization (SEM-EDS, XRD) have been performed to explain the solidification sequence, microstructure development and especially formation of the intermetallic Mg₃Bi₂ phase.

When extruding the casted rods from EN AW 2011 aluminium alloys, not only their homogenized structure, but also their extrudable properties were significantly influenced by the hardness of the alloy. In this study, the object of investigations was the EN AW 2011 aluminium alloy, and the effect of homogenisation time on hardness was investigated. First, homogenisation was carried out at 520 °C for different times, imitating industrial conditions. After homogenisation, the samples were analysed by hardness measurements and further characterised by microscopy and image analysis to verify the influence of homogenisation on the resulting microstructural constituents. In addition, non-equilibrium solidification was simulated using the program Thermo-Calc and phase formation during solidification was investigated. The homogenisation process enabled more rounded shape of the Al₂Cu eutectic phase, equilibrium formation of the phases, and the precipitation in the matrix, leading to a significant increase in the hardness of the EN AW 2011 aluminium alloy. The experimental data revealed a suitable homogenisation time of 4–6 h at a temperature of 520 °C, enabling optimal extrusion properties.