The Al coatings achieved via electrodeposition on a Cu electrode from AlCl₃-NaCl-KCl (80–10–10 wt.%) molten salts electrolyte with Tetramethylammonium Chloride (TMACl) and Sodium Iodide (NaI) additives is reported. The effect of the two additives on electrodeposition were investigated by cyclic voltammetry (CV), chronopotentiometry (CP), scanning electron microscopy (SEM) and X-ray diffraction (XRD). Results reveal that compact and smooth Al coatings are obtained at 150 °C by the electrodeposition process from the electrolyte with 1% TMACl and 10% NaI. The Al coatings exhibit great corrosion resistance close to that of pure Al plate, with a corrosion current of 3.625 μA. The average particle size is approximately 2 ± 1 μm and the average thickness of the Al layer is approximately 7 ± 2 μm. The nucleation/growth process exhibits irrelevance with TMACl or NaI during the electrodeposition of Al. TMACl cannot affect and improve the electrodeposition effectively. However, the addition of TMACl and NaI can intensify the cathodic polarization, producing an inhibition of Al deposition, and contribute to form uniform Al deposits. This can increase the conductivity and facilitate in refining the size of Al particles, contributing to forming a continuous, dense and uniform layer of Al coating, which can be used as effective additives in molten salts electrolyte.

A method of forming an Mg/Al intermetallic compound coating enriched with Mg₁₇Al₁₂ and Mg₂Al₃ was developed by heat treatment of electrodeposition Al coatings on Mg alloy at 350 °C. The composition of the Mg/Al intermetallic compounds could be tuned by changing the thickness of the Zn immersion layer. The morphology and composition of the Mg/Al intermetallic compound coatings were characterized using scanning electron microscopy (SEM), X-ray diffraction (XRD), and electron backscattered diffraction (EBSD). Nanomechanical properties were investigated via nano-hardness (nHV) and the elastic modulus (EIT), and the corrosion behavior was studied through hydrogen evolution and potentiodynamic (PD) polarization. The compact and uniform Al coating was electrodeposited on the Zn-immersed AZ91D substrate. After heat treatment, Mg₂Al₃ and Mg₁₇Al₁₂ phases formed, and as the thickness of the Zn layer increased from 0.2 to 1.8 μm, the ratio of Mg₂Al₃ and Mg₁₇Al₁₂ varied from 1:1 to 4:1. The nano-hardness increased to 2.4 ± 0.5 GPa and further improved to 3.5 ± 0.1 GPa. The Mg/Al intermetallic compound coating exhibited excellent corrosion resistance and had a prominent effect on the protection of the Mg alloy matrix. The control over the ratio of intermetallic compounds by varying the thickness of the Zn immersion layer can be an effective approach to achieve the optimal comprehensive performance. As the Zn immersion time was 4 min, the obtained intermetallic compounds had relatively excellent comprehensive properties.