In this work, Eucommia ulmoides leaf extract (EUOLstabilized silver nanoparticles (EUOL@AgNPs) incorporated sulfonated polyether sulfone (SPES)/polyethersulfone (PES) electrospun nanofiber membranes (SP ENMs) were prepared by electrospinning, and they were studied for the removal of lead (Pb(II)) and cadmium (Cd(II)) ions from aqueous solutions. The SP ENMs with various EUOL@AgNPs loadings were characterized by X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscope, thermo-gravimetric analysis (TGA), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and contact angle (CA) measurements. The adsorption studies showed that the adsorption of Cd(II) and Pb(II) was rapid, achieved equilibrium within 40 min and 60 min, respectively and fitted with non-linear pseudo-second-order (PSO) kinetics model. For Cd(II) and Pb(II), the Freundlich model described the adsorption isotherm better than the Langmuir isotherm model. The maximum adsorption capacity for Cd(II) and Pb(II) was 625 and 370.37 mg g⁻¹ respectively at neutral pH. Coexisting anions of fluoride, chloride, and nitrate had a negligible influence on Cd(II) removal than the Pb(II). On the other hand, the presence of silicate and phosphate considerably affected Cd(II) and Pb(II) adsorption. The recyclability, regeneration, and reusability of the fabricated EUOL@AgNPs-SP ENMs were studied and they retained their high adsorption capacity up to five cycles. The DFT measurements revealed that SP-5 ENMs exhibited the highest adsorption selectivity for Cd(II) and the measured binding energies for Cd(II), Pb(II), are 219.35 and 206.26 kcal mol⁻¹, respectively. The developed ENM adsorbent may find application for the removal of heavy metals from water.

As a kind of eco-friendly (biodegradable) material and with a natural anti-fouling ability, cellulose acetate (CA) is more suitable for single-use membrane (especially in bioprocess). In this study, the method for preparing CA membrane by Vapor-assisted Nonsolvent Induced Phase Separation (VNIPS) was studied. The influences of ratio compositions (solid content, acetone/N,N-Dimethylacetamide ratio, glycerol/CA ratio) and membrane preparation conditions (evaporation time, evaporation temperature and humidity) on the microstructure and other properties were systematically evaluated. Results indicated that acetone/N,N-Dimethylacetamide ratio and glycerol/CA ratio had great influence on the cross-section structure of membranes. Additionally, the membrane with homogeneous sponge-like porous structure could be prepared stably within certain limits of ratios. Under the premise of keeping the content of other components fixed, the separation membrane with a full sponge pore structure can be obtained when the ratio of glycerol/CA is ≥2.5 or the acetone/solvent ratio is between 0.25 and 0.5. Evaporation time and temperature, humidity and other membrane preparation conditions mainly affected the surface morphology and the pore size. This kind of high-performance membrane with homogeneous sponge-like pore and controllable surface morphology could be potentially used for bioseparation processes.

Using an environmentally friendly approach for eliminating methylene blue from an aqueous solution, the authors developed a unique electrospun nanofiber membrane made of a combination of polyethersulfone and hydroxypropyl cellulose (PES/HPC). SEM results confirmed the formation of a uniformly sized nanofiber membrane with an ultrathin diameter of 168.5 nm (for PES/HPC) and 261.5 nm (for pristine PES), which can be correlated by observing the absorption peaks in FTIR spectra and their amorphous/crystalline phases in the XRD pattern. Additionally, TGA analysis indicated that the addition of HPC plays a role in modulating their thermal stability. Moreover, the blended nanofiber membrane exhibited better mechanical strength and good hydrophilicity (measured by the contact angle). The highest adsorption capacity was achieved at a neutral pH under room temperature (259.74 mg/g), and the pseudo-second-order model was found to be accurate. In accordance with the Langmuir fitted model and MB adsorption data, it was revealed that the adsorption process occurred in a monolayer form on the membrane surface. The adsorption capacity of the MB was affected by the presence of various concentrations of NaCl (0.1–0.5 M). The satisfactory reusability of the PES/HPC nanofiber membrane was revealed for up to five cycles. According to the mechanism given for the adsorption process, the electrostatic attraction was shown to be the most dominant in increasing the adsorption capacity. Based on these findings, it can be concluded that this unique membrane may be used for wastewater treatment operations with high efficiency and performance.

Membrane materials might be used for face protection because they can decontaminate the inhaled air from particle pollution and viruses like the SARS-Cov0-2 which damages our respiration system. In this study, plyethersulfone membranes (PES) were synthesized with green solvent at room temperature and its filtration effectiveness was investigated against nano-bacteria (size 0.05 to 0.2 µm) by measuring their Bacterial Filtration Efficiency (BFE) and micro aerosol size (0.3 µm), and Particulate Filtration Efficiency (PFE). The average SARS-CoV-2 diameters are between 50 nm to 160 nm. A series of experiments were performed to accomplish between 0.03 to 0.21 µm PES sponge like diameters so that can be used for SARS-CoV-2 filtration. Results showed that nanofiltration/ultrafiltration could filter 99.9% of bacteria and aerosol from contaminated air the size of the Covid-19 molecule. Graphical Abstract

This study introduces an innovative approach to enhancing membrane distillation (MD) performance by developing bead-containing superhydrophobic sulfonated polyethersulfone (SPES) nanofibers with S-MWCNTs. By leveraging SPES’s inherent hydrophobicity and thermal stability, combined with a nanostructured fibrous configuration, we engineered beads designed to optimize the MD process for water purification applications. Here, oxidized hydrophobic S-MWCNTs were dispersed in a SPES solution at concentrations of 0.5% and 1.0% by weight. These bead membranes are fabricated using a novel electrospinning technique, followed by a post-treatment with the hydrophobic polyfluorinated grafting agent to augment nanofiber membrane surface properties, thereby achieving superhydrophobicity with a water contact angle (WCA) of 145 ± 2° and a higher surface roughness of 512 nm. The enhanced membrane demonstrated a water flux of 87.3 Lm⁻² h⁻¹ and achieved nearly 99% salt rejection efficiency at room temperature, using a 3 wt% sodium chloride (NaCl) solution as the feed. The results highlight the potential of superhydrophobic SPES nanofiber beads in revolutionizing MD technology, offering a scalable, efficient, and robust membrane for salt rejection.