A new decohesion element with the capability of dealing with crack propagation under mixed-mode loading is proposed and demonstrated. The element is used at the interface between solid finite elements to model the initiation and non-self-similar growth of delaminations in composite materials. A single relative displacement-based damage parameter is applied in a softening law to track the damage state of the interface and to prevent the restoration of the cohesive state during unloading. The softening law is applied in the three-parameter Benzeggagh-Kenane mode interaction criterion to predict mixed-mode delamination propagation. To demonstrate the accuracy of the predictions, steady-state delamination growth is simulated for quasi-static loading of various single mode and mixed-mode delamination test specimens and the results are compared with experimental data.

The effect of the adhesive thickness on the bond strength of single-lap adhesive joints is still not perfectly understood. The classical elastic analyses predict that the strength increases with the adhesive thickness, whereas experimental results show the opposite. Various theories have been proposed to explain this discrepancy, but more experimental tests are necessary to understand all the variables. The objective of the present study was to assess the effect of the adhesive thickness on the strength of single-lap joints for different kinds of adhesives. Three different adhesives were selected and tested in bulk. The strain to failure in tension ranged from 1.3% for the most brittle adhesive to 44% for the most ductile adhesive. The adherend selected was a high-strength steel to keep the adherends in the elastic range and simplify the analysis. Three thicknesses were studied for each adhesive: 0.2, 0.5, and 1 mm. A statistical analysis of the experimental results shows that the lap shear strength increases as the bondline gets thinner and the adhesive gets tougher.