Titanium and its alloys have become the most attractive implant materials due to their high corrosion resistance, excellent biocompatibility and relatively low elastic modulus. However, the current Ti materials used for implant applications exhibit much higher Young’s modulus (50 ~ 120 GPa) than human bone (~30 GPa). This large mismatch in the elastic modulus between implant and human bone can lead to so-called “stress shielding effect” and eventual implant failure. Therefore, the development of β-type Ti alloys with modulus comparable to that of human bone has become an ever more pressing subject in the area of advanced biomedical materials. In this study, an attempt was made to produce a bone-compatible metastable β-type Ti alloy. By alloying and thermo-mechanical treatment, a metastable β-type Ti-33Nb-4Sn (wt. %) alloy with ultralow Young’s modulus (36 GPa, versus ~30 GPa for human bone) and high ultimate strength (853 MPa) was fabricated. We believe that this method can be applied to developing advanced metastable β-type titanium alloys for implant applications. Also, this approach can shed light on design and development of novel β-type titanium alloys with large elastic limit due to their high strength and low elastic modulus.

To address the issue of high fracture and wear failure rates caused by the lack of toughness and abrasion resistance in the steel used for soil-engaging components of tillage machinery, a novel composite heat treatment process, “normalizing and intercritical quenching and tempering (NIQT)”, is proposed. By regulating the austenitizing heating temperature in the intercritical area (ferrite/austenite two-phase area), the type, content, and distribution of phases in the 27MnCrB5 test sample could be precisely controlled, which further influenced the mechanical properties of the material. The results demonstrated that a multiphase composite microstructure, predominantly consisting of martensite and ferrite, could be obtained in the 27MnCrB5 steel treated by the NIQT process. The results of an EBSD test indicated that the predominant type of grain boundary following the NIQT heat treatment was a high-angle grain boundary (approximately 59.5%), which was favorable for hindering crack propagation and improving the impact toughness of the material. The results of the mechanical tests revealed that, when the quenching temperature was set to 790 °C, the 27MnCrB5 steel attained excellent comprehensive mechanical properties, with a tensile strength of 1654 MPa, elongation of 10.4%, impact energy of 77 J, and hardness of 530 HV30. Compared with conventional heat treatment processes for soil-engaging components, this novel process has the potential to enhance the performance of soil-engaging components and prolong their service life.