Nanoparticles based on chitosan modified with epigallocatechin gallate (EGCG) were synthetized by nanoprecipitation (EGCG-g-chitosan-P). Chitosan was modified by free-radical-induced grafting, which was verified by Fourier transform infrared (FTIR). Furthermore, the morphology, particle size, polydispersity index, and zeta potential of the nanoparticles were investigated. The grafting degree of EGCG, reactive oxygen species (ROS) production, antibacterial and antioxidant activities of EGCG-g-chitosan-P were evaluated and compared with those of pure EGCG and chitosan nanoparticles (Chitosan-P). FTIR results confirmed the modification of the chitosan with EGCG. The EGCG-g-chitosan-P showed spherical shapes and smoother surfaces than those of Chitosan-P. EGCG content of the grafted chitosan nanoparticles was 330 μg/g. Minimal inhibitory concentration (MIC) of EGCG-g-chitosan-P (15.6 μg/mL) was lower than Chitosan-P (31.2 μg/mL) and EGCG (500 μg/mL) against Pseudomonas fluorescens (p < 0.05). Additionally, EGCG-g-chitosan-P and Chitosan-P presented higher Staphylococcus aureus growth inhibition (100%) than EGCG at the lowest concentration tested. The nanoparticles produced an increase of ROS (p < 0.05) in both bacterial species assayed. Furthermore, EGCG-g-chitosan-P exhibited higher antioxidant activity than that of Chitosan-P (p < 0.05) in 2,2′-azino-bis (3-ethyl-benzothiazoline-6-sulfonic acid) (ABTS), 2,2-diphenyl-1-picrylhydrazyl radical (DPPH) and ferric-reducing antioxidant power assays. Based on the above results, EGCG-g-chitosan-P shows the potential for food packaging and biomedical applications.

Benefits of nanotechnology in agriculture include reduced fertilizer loss, improved seed germination rate and increased crops quality and yield. The objective of this research was to evaluate the effects of zinc oxide nanoparticles (ZnO-NPs), at 1500 ppm, on tomato (Solanum lycopersicum L.) growth. ZnO-NPs were synthetized to produce either spherical or hexagonal morphologies. In this research, we also studied two application methods (foliar and drench) and nanoparticles’ (NPs) surface modification with maltodextrin. The results obtained indicate that ZnO-NP-treated tomato plants significantly increased plant height, stem diameter and plant organs (leaves, stem and root) dry weight compared to plants without NP treatment.

The main difference between microwave (MW) and conventional heating is the way heat is transferred, since the MW energy interacts directly with the material and it can be absorbed, transmitted, or reflected by the surface, while conventional heating proceeds through a conduction transfer heat. Natural fibers (NF) have been modified by MW treatment, and they can be useful in the development of polymeric biocomposites, biofuels, activated carbon and carbon nanostructures. This review summarizes the advances of MW radiation treatments on NF. Additionally, the relationship among the MW reactor design, MW processing conditions (temperature, time treatment, and radiated power) to the dielectric (Tan δ) properties of each fiber component (cellulose, lignin, and hemicellulose) was assessed in this paper. Furthermore, an overview of the main morphological and structural changes of NF after MW treatment is presented with the objective of suggesting processing methodologies that will increase the reproducibility data, as well as the functionality, applications and industrial process scale-up of the NF.

The performance of Polyethylene (PE)/Clay/Silver nanocomposites is dependent to a great extent on the properties of filler–matrix interface. To improve the interfacial properties in PE/Clay/Silver composites, different types of compatibilizers or adhesion promoters were introduced. The compatibilization provided by maleic anhydride (MA), itaconic acid (IA) and 2-[2-(dimethylamine)-ethoxy] ethanol (DMAE) functionalized PEs for forming PE-based nanocomposites was studied and compared. IA was grafted into PE by melt mixing to obtain PEgIA (compatibilizer 1), thereafter, PEgIA and PEgMA (compatibilizer 2) were reacted with DMAE also by melt mixing to obtain PEgI-DMAE (compatibilizer 3) and PEgM-DMAE (compatibilizer 4). These compatibilizers were reacted using ultrasound with a solution of AgNO₃ 0.04 M and ethylene glycol. Ammonium hydroxide was added in a ratio of 2:1 M with respect to silver nitrate. These silver coated compatibilizers were mixed with PE and with a quaternary ammonium modified montmorillonite clay (Nanomer I28E), thus forming the different hybrid PE/Clay/Silver nanocomposites. FTIR confirmed the formation of these compatibilizers. All the DMAE compatibilized nanocomposites had better filler (clay and silver) dispersion and exfoliation. XRD, oxygen and water transmission rate as well as antimicrobial properties attained showed that the PEgI-DMAE produced the better dispersed PE, clay and silver nanocomposites. The obtained nanocomposites showed enhanced barrier properties and outstanding antimicrobial properties against bacteria, E. coli. PEgI-DMAE offers an outstanding capability for preparing nanocomposites with highly exfoliated and dispersed filler into the PE matrix that offers a new option for obtaining hybrid nanocomposites with enhanced properties to be used in packaging applications.