In the search for applications for alloys developed under the philosophy of the High Entropy Alloy (HEA)-type materials, the focus may be placed on applications where current alloys also use multiple components, albeit at lower levels than those found in HEAs. One such area, where alloys with complex compositions are already found, is in filler metals used for joining. In soldering (450 °C), filler metal alloys are taken above their liquidus temperature and used to form a metallic bond between two components, which remain both unmelted and largely unchanged throughout the process. These joining methods are widely used in applications from electronics to aerospace and energy, and filler metals are highly diverse, to allow compatibility with a broad range of base materials (including the capability to join ceramics to metals) and a large range of processing temperatures. Here, we review recent developments in filler metals relevant to High Entropy materials, and argue that such alloys merit further exploration to help overcome a number of current challenges that need to be solved for filler metal-based joining methods.

The formation of entrainment defects, (also known as double oxide film defects or bifilms), caused by the entrapment of a doubled-over surface oxide film containing a small amount of local atmosphere, has been investigated by combining practical experiments using a commercial-purity Mg-alloy under protective gases, with theoretical thermodynamic calculations. Evolution of the entrainment defects was studied, and a double-layered structure of their oxide films was found, which was different from the single-layered structure of the Mg-alloy melt surface films that have been previously reported. A pore gas analyzer was used to analyze the gas trapped within the defects from which H₂ and N₂ (from the air) were detected. It was found that entrapped gases can be depleted through reactions with the surrounding liquid Mg-alloy, resulting in the oxide films growing together in the melt. Transformation of the entrained gas to solid-phase compounds could reduce the void volume of the defects, thus probably diminishing the negative effect of the entrainment defects on the quality of castings.