3D carbon-based structures have proven useful for tailoring material properties in structural mechanical and energy storage applications. One approach to obtain them has been by carbonization of selected metal-organic frameworks (MOFs) with catalytic metals, but this is not applicable to most common MOF structures. Here, we present a strategy to transform common MOFs, by guest inclusions and high-temperature MOF-guest interactions, into complex carbon-based, diatom-like, hierarchical structures (named for the morphological similarities with the naturally-existing dia-tomaceous species). As an example, we introduce metal salt guests into HKUST-1-type MOFs to generate a family of carbon-based nano-diatoms with two-to-four levels of structural hierarchy. We report control of the morphology by simple changes in the chemistry of the MOF and guest, with implications for the formation mechanisms. We demonstrate that one of these structures has unique advantages as a fast-charging Li-ion battery (LiB) anode. The tunability of composition should enable further studies of reaction mechanisms and result in the growth of a myriad of unprecedented carbon-based structures from the enormous variety of currently-available MOF-guest candidates.

Conducting polymers show great promise as supercapacitor materials due to their high theoretical specific capacitance, low cost, toughness, and flexibility. Poor ion mobility, however, can render active material more than a few tens of nanometers from the surface inaccessible for charge storage, limiting performance. Here, we use semi-interpenetrating networks (sIPNs) of a pseudocapacitive polymer in an ionically conductive polymer matrix to decrease ion diffusion length scales and make virtually all of the active material accessible for charge storage. Our freestanding poly(3,4-ethylenedioxythiophene)/poly(ethylene oxide) (PEDOT/PEO) sIPN films yield simultaneous improvements in three crucial elements of supercapacitor performance: specific capacitance (182 F/g, a 70% increase over that of neat PEDOT), cycling stability (97.5% capacitance retention after 3000 cycles), and flexibility (the electrodes bend to a <200 μm radius of curvature without breaking). Our simple and controllable sIPN fabrication process presents a framework to develop a range of polymer-based interpenetrated materials for high-performance energy storage technologies.

Lithium (Li) metal is a promising anode material for lithium-ion batteries (LIBs) because of its high theoretical specific capacity of 3860 mAh g^-1 and the low potential of -3.04 V versus the standard hydrogen electrode (SHE). However, these anodes rely on repeated plating and stripping of Li, which leads to consumption of Li inventory and the growth of dendrites that can lead to self-discharge and safety issues. To address these issues, as well as problems related to the volume change of these anodes, a number of different porous conductive scaffolds have been reported to create high surface area electrode on which Li can be plated reliably. While impressive results have been reported in literature, current processes typically rely on either expensive or poorly scalable techniques. Herein, we report a scalable fabrication method to create robust 3D Cu anodes using a one-step electrodeposition process. The areal loading, pore structure, and electrode thickness can be tuned by changing the electrodeposition parameters, and we show how standard mechanical calendering provides a way to further optimize electrode volume, capacity, and cycling stability. Optimized electrodes achieve high Coulombic efficiencies (CEs) of 99% during 800 cycles in half cells at a current density of 0.5 mA cm^-2 with a total capacity of 0.5 mAh cm^-2. To the best of our knowledge, this is the highest value ever reported for a host for Li-metal anodes using lithium bis(trifluoromethanesulfonyl)imide LITFSI based electrolyte.