This manuscript investigates the structural and electrical properties of a Ba_0.75Bi_0.25Ni_0.7Mn_0.3O₃ (BNMO) perovskite compound synthesized through the sol–gel method.

The ZnO-based visible-LED photocatalytic degradation and mineralization of two typical cyanotoxins, microcystin-LR (MC-LR), and anatoxin-A were examined. Al-doped ZnO nanoparticle photocatalysts, in Al:Zn ratios between 0 and 5 at.%, were prepared via sol-gel method and exhaustively characterized by X-ray diffraction, transmission electron microscopy, UV-vis diffuse reflectance spectroscopy, photoluminescence spectroscopy, and nitrogen adsorption-desorption isotherms. With both cyanotoxins, increasing the Al content enhances the degradation kinetics, hence the use of nanoparticles with 5 at.% Al content (A5ZO). The dosage affected both cyanotoxins similarly, and the photocatalytic degradation kinetics improved with photocatalyst concentrations between 0.5 and 1.0 g L⁻¹. Nevertheless, the pH study revealed that the chemical state of a species decisively facilitates the mutual interaction of cyanotoxin and photocatalysts. A5ZO nanoparticles achieved better outcomes than other photocatalysts to date, and after 180 min, the mineralization of anatoxin-A was virtually complete in weak alkaline medium, whereas only 45% of MC-LR was in neutral conditions. Moreover, photocatalyst reusability is clear for anatoxin-A, but it is adversely affected for MC-LR.

The ceramic Sr(NiNb)_0.5O₃, incorporating silver doping in the A site, was synthesized using a sol–gel route and subjected to comprehensive analysis through various experimental techniques. X-ray diffraction data analysis indicates a rhombohedral crystal structure. Scanning electron microscopy (SEM) examination reveals densely packed grains with minimal surface porosity. A thorough investigation of electrical properties, encompassing dielectric constant, loss tangent, electrical impedance, modulus, conductivity, etc., was conducted across a wide frequency range (10³–10⁶ Hz) and temperature range (260–340 K). This analysis provided valuable insights into structure–property relationships and conduction mechanisms. The discussion highlights the significance of interface effects, space charge polarization, and Maxwell–Wagner dielectric relaxation in achieving the material’s high dielectric constant at low frequencies and elevated temperatures. Examination of temperature dependence through Nyquist plots elucidates the contributions of grain behavior to the material’s resistive and capacitive properties. The dielectric permittivity, dissipation of energy, and electrical characteristics like impedance, modulus and conductivity are notably influenced by the frequency of the applied electric field and temperature. Overall, the material exhibits promising potential for industrial applications such as energy storage, given its intriguing properties.

In this study, Cu-doped ZnO aerogel nanoparticles with a 4% copper concentration (Cu4ZO) were synthesized using a sol–gel method, followed by supercritical drying and heat treatment. The subsequent fabrication of Cu4ZO ceramics through Spark Plasma Sintering (SPS) was characterized by X-ray diffraction (XRD), field-emission gun scanning electron microscopy (FE-SEM) equipped with EDS, and impedance spectroscopy (IS) across a frequency range of 100 Hz to 1 MHz and temperatures from 270 K to 370 K. The SPS–Cu4ZO sample exhibited a hexagonal wurtzite structure with an average crystallite size of approximately 229 ± 10 nm, showcasing a compact structure with discernible pores. The EDS spectrum indicates the presence of the base elements zinc and oxygen with copper like the dopant element. Remarkably, the material displayed distinct electrical properties, featuring high activation energy values of about 0.269 ± 0.021 eV. Complex impedance spectroscopy revealed the impact of temperature on electrical relaxation phenomena, with the Nyquist plot indicating semicircular arc patterns associated with grain boundaries. As temperature increased, a noticeable reduction in the radius of these arcs occurred, coupled with a shift in their center points toward the axis center, suggesting a non-Debye-type relaxation mechanism. Dielectric analyses revealed a temperature-driven evolution of losses, emphasizing the material’s conductivity impact. Non-Debye-type behavior, linked to ion diffusion, sheds light on charge storage dynamics. These insights advance potential applications in electronic devices and energy storage.

Pure zinc oxide nanoparticles, as well as those doped with 3% calcium, aluminum, and gallium, were synthesized using a sol–gel method and then deposited onto an alumina substrate for sensing tests. The resulting nanoparticles were characterized using a variety of techniques, including X-ray diffraction (XRD), scanning electron microscopy (SEM) equipped with energy dispersive X-ray analysis (EDX), transmission electron microscopy (TEM), UV-VIS-NIR absorption spectroscopy, and photoluminescence (PL) measurements, to examine their structural, morphological, and optical properties. The prepared nanoparticles were found to have the hexagonal wurtzite structure of ZnO with a P63mC space group. The UV-Vis-IR spectra showed that the samples are highly absorbent in the UV range, while the PL spectra confirmed the presence of many defects in the ZnO structure, such as oxygen vacancies and zinc interstitials. The doped samples exhibited more defects than the pure sample. SEM images of the deposited film surface showed agglomerates with a spherical shape and confirmed the nanometer scale size of our prepared samples, as corroborated by the TEM images. The EDX spectra indicated the high purity of the ZnO deposited films, with a high presence of Zn and O and the presence of the doped elements (Ca, Al, and Ga) in each doped sample. Sensing tests were performed on ZnO, Ca_3%-doped ZnO (C3ZO), Al_3%-doped ZnO (A3ZO), and Ga_3%-doped ZnO (G3ZO) sensors in the presence of volatile organic compounds (VOCs) gases such as ethanol, formaldehyde, methanol, and acetone at low concentrations. The sensors exhibited high responses to low ppm level concentrations of the VOCs gases. At a low operational temperature of 250 °C, the C3ZO sensor had the highest response to 5 ppm of ethanol, methanol, and formaldehyde gases compared to the pure and other doped sensors. Additionally, the A3ZO sensor exhibited the highest response to acetone gas. In conclusion, our findings suggest that the doping of zinc oxide can enhance the low concentration detection of VOCs gases, with the C3ZO and A3ZO sensors showing the highest response to specific gases.