The goal of this study was to optimize the activation behaviour of hydrogen storage alloy TiFe. We found that the addition of a small amount of Zr in TiFe alloy greatly reduces the hydrogenation activation time. Two different procedural synthesis methods were applied: co-melt, where the TiFe was melted and afterward re-melted with the addition of Zr, and single-melt, where Ti, Fe and Zr were melted together in one single operation. The co-melted sample absorbed hydrogen at its maximum capacity in less than three hours without any pre-treatment. The single-melted alloy absorbed its maximum capacity in less than seven hours, also without pre-treatment. The reason for discrepancies between co-melt and single-melt alloys was found to be the different microstructure. The effect of air exposure was also investigated. We found that the air-exposed samples had the same maximum capacity as the argon protected samples but with a slightly longer incubation time, which is probably due to the presence of a dense surface oxide layer. Scanning electron microscopy revealed the presence of a rich Zr intergranular phase in the TiFe matrix, which is responsible for the enhanced hydrogenation properties of these Zr-doped TiFe alloys.

We report here the effect on hydrogen sorption behavior of replacing vanadium by ferrovanadium (FeV) in Ti-V-Cr Body Centred Cubic (BCC) solid solution alloys. The compositions studied were Ti_1.56V_0.36Cr_1.08 and Ti_1.26V_0.63Cr_1.11. Both of the alloys were synthesized by melting with 4 wt % of Zr₇Ni₁₀ in order to enhance the first hydrogenation (i.e., activation) kinetics. The ferrovanadium substitution leads to the same microstructure as the vanadium pristine alloys and no significant change in the lattice parameters was found. However, a longer incubation time was observed in the activation process for the FeV substituted alloy. Finally, the replacement of vanadium by ferrovanadium did not have a noticeable impact on the hydrogen capacities, heat of formation, and entropy.