The behaviour of reinforced concrete frames with masonry wall infills is influenced a lot by the stiffness and strength difference between the frame and the infill, causing early detrimental damage to the infill or to the critical concrete columns. The paper reports the results from shake table seismic tests on a full-scale reinforced concrete (RC) frame building with modified hollow clay block (orthoblock brick) infill walls, within INMASPOL SERA Horizon 2020 project. The building received innovative resilient protection using Polyurethane Flexible Joints (PUFJs) made of polyurethane resin (PU), applied at the frame-infill interface in different schemes. Further, PUs were used for bonding of glass fibre grids to the weak masonry substrate to form Fibre Reinforced Polyurethanes (FRPUs) as an emergency repair intervention. The test results showed enhancement in the in-plane and out-of-plane infill performance under seismic excitations. The results confirmed remarkable delay of significant infill damages at very high RC frame inter-story drifts as a consequence of the use of PUFJs. Further, the PUFJ protection enabled the resilient repair of the infill even after very high inter-story drift of the structure up to 3.7%. The applied glass FRPU system efficiently protected the damaged infills against collapse under out-of-plane excitation while they restored large part of their in-plane stiffness.

Rock mass fractures adversely affect the production of ornamental stone quarries. Fractures cause natural rock blocks, which threaten extraction of the required commercial block size of ornamental stones. Accurate subsurface detection and modeling of fractures are required for pre-exploitation evaluation and planning. This paper introduces a new three-dimensional deterministic fracture modeling approach using ground penetrating radar (GPR) as a data acquisition tool. A case study was performed in a fractured bench of a sandstone quarry in Firenzuola, Italy, using a 400 MHz GPR antenna. To accurately detect fractures at true depth, an in situ calibration based on previous knowledge of the depth of a subsurface reference reflector allowed us to estimate a bulk dielectric constant of the rock mass during the time of data acquisition. A data interpretation tracing technique was developed to model fractures as 3-D surfaces in two forms, either irregular or planes. The modeled fractures were visualized through a multi-platform visualization software package (ParaView). A comparison between the orientations of the fractures measured by the traditional manual method and the orientations of the modeled fractures is presented as a possible geologic validation for the detection and interpretation of fractures. For the objective of pre-exploitation evaluation, a distribution analysis provided an evaluation-based fracture index for the bench in the case study.

In masonry materials, the superficial decay is a widespread problem. Aggressive environmental agents such as moisture and salts trigger the damage by propagating through the material capillary pores. Although several studies have been carried out on salt crystallization and their damaging effects, additional research effort is required to better investigate this phenomenon on real cases and real weathering conditions. To this purpose, testing and monitoring tools capable of following degradation process since the early beginning are necessary. Repeated visual inspections are commonly used to monitor the superficial decay, but this technique is subjective and thus not capable of providing any quantitative information. In this work, an experimental campaign, carried out in Bologna, Italy, is presented. A two-header brick wall, one main face unplastered and one plastered, was stored outdoors and exposed to weathering over two summers. Before the start of the second aging season, moisture and salt capillary rise was simulated by low-concentrated sodium chloride solution (0.1% -wt). The aim was to favor solution evaporation and salt crystallization and to provoke material damage. The degradation process was monitored based on a contactless, rapid and accurate image diagnostic technique. In particular, high-resolution laser scanning by triangulation technique was adopted. Three-dimensional data acquisition was repeated at the end of both seasons. The proposed procedure successfully extracted quantitative information approximately areas of material spalling and detachment even in the initial phases of decay.