Bamboo scrimber is one of the most popular engineering bamboo composites, owing to its excellent physical and mechanical properties. In order to investigate the influence of grain direction on the compression properties and failure mechanism of bamboo scrimber, the longitudinal, radial and tangential directions were selected. The results showed that the compressive load–displacement curves of bamboo scrimber in the longitudinal, tangential and radial directions contained elastic, yield and failure stages. The compressive strength and elastic modulus of the bamboo scrimber in the longitudinal direction were greater than those in the radial and tangential directions, and there were no significant differences between the radial and tangential specimens. The micro-fracture morphology shows that the parenchyma cells underwent brittle shear failure in all three directions, while the fiber failure of the longitudinal compressive specimens consisted of ductile fracture, and the tangential and radial compressive specimens exhibited brittle fracture. This is one of the reasons that the deformation of the specimens under longitudinal compression was greater than those under tangential and radial compression. The main failure mode of bamboo scrimber under longitudinal and radial compression was shear failure, and the main failure mode under tangential compression was interlayer separation failure. The reason for this difference was that during longitudinal and radial compression, the maximum strain occurred at the diagonal of the specimen, while during tangential compression, the maximum strain occurred at the bonding interface. This study can provide benefits for the rational design and safe application of bamboo scrimber in practical engineering.

As a green and low-carbon natural polymer material, wood has always been popular in engineering applications owing to its excellent physical and mechanical properties. In this study, compression tests in conjunction with in situ test methods (DIC method) were used to investigate the compression mechanism of wood samples in the longitudinal, radial, and tangential directions. The macroscopic failure modes, energy dissipation results, and variations in the strain field were analyzed. The results showed that the load–displacement curve in each grain orientation included three stages: an elasticity stage, yield stage, and strengthening stage. Both the compressive strength and elastic modulus in the longitudinal direction were significantly higher than those in the radial and tangential directions, but there was no significant difference between the radial and tangential directions. Specimens in the longitudinal direction mainly presented fiber buckling, fiber shear slippage, and fiber fracture failure; in radial directions mainly presented compression compaction of the fiber cells; and in the tangential directions presented buckling and shear failure of the laminar layers. The energy absorption in the longitudinal direction was better than in the other directions. The strain changed significantly in the loading direction in the elastic stage while the shear strain changed remarkably in the yield stage in each grain orientation. In this paper, the compression mechanical properties of larch wood in different grain orientations were studied to provide a reference for its safe application in engineering.

To further verify the feasibility of newly designed reinforced bamboo scrimber composite (RBSC) beams used in building construction, the bonding properties between steel bar and bamboo scrimber were investigated by anti-pulling tests. Results indicated that the anti-pulling mechanical properties were signifi- cantly correlated to the diameter, thread form and buried depth of steel bar, forming density of bamboo scrimber as well as the heat treatment of bamboo bundle. There were two failure modes for anti-pulling tests: the tensile fracture and pulling out of steel bar. Both the ultimate load and average shear strength of anti-pulling specimen could be increased greatly with the ribbed bar, high forming density of bamboo scrimber and un-heated bamboo bundle. Furthermore, a theoretical calculation model of the bonding interface between steel bar and bamboo scrimber was developed. Based on the theoretical calculation model, the change laws of normal stress of bamboo scrimber, and shear stress of glue layer along the buried depth of steel bar were revealed. This study is beneficial for the safety application of RBSC beams in building construction.

As a modern bamboo composite with good mechanical properties, bamboo scrimber (BS) has achieved prominence in the sustainable architecture field. When used as a structural material, it is inevitably under continual tension perpendicular to the grain, therefore its mechanical response under long-term loading is significant for structural design. In this study, tensile tests were conducted on BS under short-term and long-term loads perpendicular to the grain. The duration of load (DOL) effect on BS perpendicular to grain and its creep effect were analyzed. Compared with BS parallel to the grain, the DOL effect on BS perpendicular to the grain was less severe, and the capacity for creep resistance was weaker. The threshold stress ratio and relative creep strain of BS perpendicular to the grain were 0.40 and 0.87, respectively. It was found that the DOL models and the viscoelastic model accurately predicted the DOL factor and creep strain. This study provides a scientific reference for the safe lifetime service of BS in practical engineering.