Nanopillar crystalline indium tin oxide (ITO) thin films were deposited on soda-lime glass substrates by radio frequency (RF) magnetron sputtering under the power levels of 100 W, 150 W, 200 W and 250 W. The preparation process of thin films is divided into two steps, firstly, sputtering a very thin and granular crystalline film at the bottom, and then sputtering a nanopillar crystalline film above the bottom film. The structure, morphology, optical and electrical properties of the nanopillar crystalline ITO thin films were investigated. From X-ray diffraction (XRD) analysis, the nanopillar crystalline thin films shows (400) preferred orientation. Due to the effect of the bottom granular grains, the crystallinity of the nanopillar crystals on the upper layer was greatly improved. The nanopillar crystalline ITO thin films exhibited excellent electrical properties, enhanced visible light transmittance and a highly infrared reflectivity in the mid-infrared region. It is noted that the thin film deposited at 200 W showed the best combination of optical and electrical performance, with resistivity of 1.44 × 10⁻⁴ Ω cm, average transmittance of 88.49% (with a film thickness of 1031 nm) and IR reflectivity reaching 89.18%.

Cross-flow hollow fiber membranes are commonly applied in humidification/dehumidification. Hollow fiber membranes vibrate and deform under the impinging force of incoming air and the gravity of liquid in the inner tube. In this study, fiber deformation was caused by the pulsating flow of air. With varied pulsating amplitudes and frequencies, single-fiber deformation was investigated numerically using the fluid–structure interaction technique and verified with experimental data testing with a laser vibrometer. Then, the effect of pulsating amplitude and frequency on heat and mass transfer performance of the hollow fiber membrane was analyzed. The maximum fiber deformation along the airflow direction was far larger than that perpendicular to the flow direction. Compared with the case where the fiber did not vibrate, increasing the pulsation amplitude could strengthen Nu by 14–87%. Flow-induced fiber vibration could raise the heat transfer enhancement index from 13.8% to 80%. The pulsating frequency could also enhance the heat transfer of hollow fiber membranes due to the continuously weakened thermal boundary layer. With the increase in pulsating amplitude or frequency, the Sh number or E_m under vibrating conditions can reach about twice its value under non-vibrating conditions.