Geopolymer concrete (GC), also known as green concrete, contains slag, silica fume, and fly ash as binders. The absence of cement in concrete is critical to protect the world from the environmental impacts of cement production. In addition, exposure to high temperatures is a critical parameter that causes loss of strength in concrete. In this study, Geopolymer concrete samples were prepared with 10 different samples containing different proportions of slag, silica fume, and porous ash and subjected to various physical, mechanical, and optical tests. The sample (GS90) with optimum workability and compressive strength, which also showed high performance in water absorption, freeze-thaw, and UPV tests, was used in high-temperature tests. Portland cement concrete (PCC) was used as a control sample. This study investigated the effect of high temperatures on the physical and mechanical properties of fiber-free GCs containing 2%, 5%, and 10% by volume of ceramic fibers. Therefore, fiber-reinforced, fiber-free, and PCC specimens were subjected to high-temperature tests at 100, 300, 600, and 900 °C. As a result of the observation of crack growth, color changes, and compressive strength parameters in the samples subjected to high-temperature tests, the thermal resistance of the 10% ceramic fiber geopolymer concrete sample was 2.5% higher than other samples. There is no study in the literature that examines the behavior of ceramic fiber-reinforced geopolymer concrete at high temperatures. This research revealed an important finding by proving that ceramic fiber reinforcement increases the compressive strength of geopolymer concretes at a remarkable rate after high-temperature impact.

Geopolymer concretes a substitute for traditional Portland cement as a more environmentally sustainable alternative. In addition, one of the most significant advantages of geopolymer concrete is the high setting speed that can be achieved with thermal curing, that is, the short curing period. Research on geopolymer concrete has focused on curing, where curing is usually done with conventional ovens. Microwave curing initiates heat generation at the molecular level, which results in a minimal heat increase on the surface of the specimens compared to traditional thermal curing methods. In addition, it provides internal, rapid, and homogeneous heating and rapid strength development. This study is based on research that examined the effect of microwave cure on the compressive strength of silica füme-modified geopolymer mortar. In the study, sodium silicate and sodium hydroxide were used for activation, and first of all, fly ash substituted geopolymer mortar specimens were subjected to conventional thermal curing in an oven. On the other hand, the mortar specimens with the same composition were subjected to short-duration (10 minutes) microwave curing at power levels of between 200-600 W. When the results were compared regarding compressive strength, void and percent water absorption, UPV, and SEM-internal structure examination, it was revealed that microwave curing could be used faster than the conventional oven curing method in silica füme-added fly ash-based geopolymer mortars. This research can be considered an essential step for further optimizing and popularising geopolymer concrete and microwave curing and proposes a method that should be considered in the future development of more sustainable construction materials.