The possibility of using coconut fatty acid diethanolamide, a derivate from coconut oil as a bio-based polyol for the synthesis of polyurethane foam was explored. The intrinsic tertiary amine moiety in this polyol (p-CFAD) endowed an auto-catalytic effect in the synthesis process of polyurethane foams, combined with a shorter cream and gelation time compared to the fossil-based polyol 3152. H-nuclear magnetic resonance (¹H-NMR) and Fourier transform infrared spectrometry (FTIR) were conducted to characterize the chemical structural features of the p-CFAD, and rheology measurement showed the shear-thinning behavior due to the branched structure. A thermal conductivity comparable to the commercial rigid polyurethane foam was achieved when 40wt% fossil-based polyol 3152 was substituted with the bio-based p-CFAD. With the increased content of the p-CFAD, a transition of the physical properties from rigid PU foam to soft PU foam was observed. Scanning electron microscopy (SEM) revealed the occurrence of the interconnected pores on the cell walls with the increase of the added p-CFAD, implying the possibility of regulating the cellular structure and foam properties via the incorporation of the p-CFAD. Results showed the feasibility of using p-CFAD as a potential polyol in the development of bio-based polyurethane foams with high performance.

In this study, a type of alkaline solid polyelectrolyte (ASPE) membrane was developed via the introduction of microcrystalline cellulose (MCC) and its modified product (QMCC) into the polyvinyl alcohol (PVA) matrix. In this process, green NaOH/urea-based solvent was used to achieve a good dispersion of MCC in the PVA matrix; meanwhile, the OH⁻ groups in the NaOH/urea-based solvent provided an alkaline environment for good ion conductivity. Compared to the MCC-incorporated ASPE, further improved conductivity was achieved when the MCC was modified with quantitative quaternary ammonium salt. TGA showed that the addition of QMCC improved the water retention of the matrix, which was beneficial to the OH⁻ conduction in the system. Compared to the control (50 mS cm⁻¹), a maximum conductivity of 238 mS cm⁻¹ was obtained after the incorporation of QMCC in the PVA matrix. Moreover, the tensile strength of the polymer electrolyte were also significantly increased with the addition of QMCC. Finally, this developed ASPE membrane was used in assembling a flexible Zn–air battery and showed a promising potential in the development of flexible electronic devices.

The alkali lignin-based poly(tetraethylene pentamine-pyrogallol) (AL-PTAP) was prepared with an adsorption capacity of 769.2 mg g⁻¹ and a removal percentage of almost 100% within 1 min at an initial concentration of less than 90 mg L⁻¹.