Kaolin is most often used as traditional raw material in ceramic industry. The purpose of the study was to obtain understanding of the structural and chemical variability of cordierite ceramics influenced by chemical and mineralogical properties of six raw kaolins taken from different localities when they are applied in ceramics mixtures with vermiculite and sintered up to 1300 °C. The X-ray diffraction and simultaneous thermogravimetric and differential thermal analysis were used to identify and characterize crystalline mineral phases and the course of reactions during the heating. The percentages of the crystalline and non-crystalline phases were newly determined by recalculation of the bulk chemical analyses of kaolins and cordierite ceramics using Chemical Quantitative Mineral Analysis (CQMA) method. Varying amounts of minerals in kaolins: kaolinite from 73.3 to 85.0, muscovite from 4.2 to 9.9, and quartz from 6.0 to 19.5 (mass %) affected amount of cordierite/indialite from 75.2 to 85.1, enstatite from 5.8 to 8.9 (when are calculated as their maximal possible percentages), and non-crystalline phases from 8.8 to 15.1 (mass %) in cordierite ceramics. Regression analysis predicted high relationship between quantity of: (a) kaolinite in kaolins and crystalline cordierite and (b) quartz in kaolins and non-crystalline phases in the ceramics. The migration of potassium from muscovite into the cordierite structure, melting point and crystallization of cordierite/indialite phases and pore size variability in relation to impurity of kaolins are documented and discussed.

An innovative chemical quantitative mineral analysis (CQMA) was successfully tested on a cordierite-based clay ceramic sample to quantify crystalline and amorphous components. The accuracy of this method was demonstrated on an added module to the CQMA program that used oxide formulas of amorphous phases obtained by energy dispersive X-ray spectroscopy (EDS) microprobe chemical analysis. This CQMA method was tested for three variants calculated using chemical analysis, i.e., X-ray diffraction (XRD) identification of crystalline (cordierite and enstatite) and amorphous phases by scanning electron microscopy (SEM)/EDS texture and microanalyses. The test results from CQMA suggest their application possibilities as well as the limits of their utilization.