Biocompatible and degradable dual‐delivery gel systems based on hyperbranched dendritic−linear−dendritic copolymers (HBDLDs) is herein conceptualized and accomplished via thiol‐ene click chemistry. The elasticity of the hydrogels is tunable by varying the lengths of PEG (2, 6, 10 kDa) or the dry weight percentages (20, 30, 40 wt%), and are found to range from 2–14.7 kPa, comparable to human skin. The co‐delivery of antibiotics is achieved, where the hydrophilic drug novobiocin sodium salt (NB) is entrapped within the hydrophilic hydrogel, while the hydrophobic antibiotic ciprofloxacin (CIP) is encapsulated within the dendritic nanogels (DNGs) with hydrophobic cores (DNGs‐CIP). The DNGs‐CIP with drug loading capacity of 2.83 wt% are then physically entrapped within the hybrid hydrogels through UV curing. The hybrid hydrogels enable the quick release of NB and prolonged released of CIP. In vitro cell infection assays showed that the antibiotic‐loaded hybrid hydrogels are able to treat bacterial infections with significant bacterial reduction. Hybrid hydrogel band aids are fabricated and exhibited better antibacterial activity compared with commercial antimicrobial band aids. Remarkably, most hydrogels and hybrid hydrogels show enhanced human dermal cell proliferation and could be degraded into non‐toxic constituents, showing great promise as wound dressing materials.

A novel platform of dendritic nanogels is herein presented, capitalizing on the self‐assembly of allyl‐functional polyesters based on dendritic‐linear‐dendritic amphiphiles followed by simple cross‐linking with complementary monomeric thiols via UV initiated off‐stoichiometric thiol‐ene chemistry. The facile approach enabled multigram creation of allyl reactive nanogel precursors, in the size range of 190–295 nm, being readily available for further modifications to display a number of core functionalities while maintaining the size distribution and characteristics of the master batch. The nanogels are evaluated as carriers of a spread of chemotherapeutics by customizing the core to accommodate each individual cargo. The resulting nanogels are biocompatible, displaying diffusion controlled release of cargo, maintained therapeutic efficacy, and decreased cargo toxic side effects. Finally, the nanogels are found to successfully deliver pharmaceuticals into a 3D pancreatic spheroids tumor model.

Cationic dendrimers are intriguing materials that can be used as antibacterial materials; however, they display significant cytotoxicity towards diverse cell lines at high generations or high doses, which limits their applications in biomedical fields. In order to decrease the cytotoxicity, a series of biocompatible hybrid hydrogels based on cationic dendrimers and carboxylated cellulose nanofibrils were easily synthesized by non-covalent self-assembly under physiological conditions without external stimuli. The cationic dendrimers from generation 2 (G2) to generation 4 (G4) based on trimethylolpronane (TMP) and 2,2-bis (methylol)propionic acid (bis-MPA) were synthesized through fluoride promoted esterification chemistry (FPE chemistry). FTIR was used to show the presence of the cationic dendrimers within the hybrid hydrogels, and the distribution of the cationic dendrimers was even verified using elemental analysis of nitrogen content. The hybrid hydrogels formed from G3 and G4 showed 100% killing efficiency towards Escherichia coli (E. coli), Staphylococcus aureus (S. aureus) and Pseudomonas aeruginosa (P. aeruginosa) with bacterial concentrations ranging from 10⁵ CFU/mL to 10⁷ CFU/mL. Remarkably, the hybrid hydrogels also showed good biocompatibility most probably due to the incorporation of the biocompatible CNFs that slowed down the release of the cationic dendrimers from the hybrid hydrogels, hence showing great promise as an antibacterial material for biomedical applications.

In a tri-component reaction, an electrophilically-activated perfluoroaryl azide, an aldehyde and an amine react readily to yield a stable amidine conjugate.

Bacterial infections are one of the major threats to human health due to the raising crisis of antibiotic resistance. Herein, second generation antibacterial heterofunctional dendrimers based on 2,2-bis(methylol)propionic acid were synthesized. The dendrimers possessed six alkenes and 12 ammonium end-groups per molecule and were used to fabricate antibacterial hydrogels together with dithiol-functional polyethylene glycol (mol wt of 2, 6 and 10 kDa) as crosslinkers via thiol-ene chemistry. The network formation can be completed within 10 s upon UV-irradiation as determined by the stabilization of the storage modulus in a rheometer. The hydrogels swelled in aqueous media and could be functionalized with the N-hydroxysuccinimide ester of the dye disperse red 13, which allowed for visually studying the degradation of the hydrogels through the hydrolysis of the ester bonds of the dendritic component. The maximum swelling ratio of the gels was recorded within 4–8 h and the swelling ratios increased with higher molecular weight of the polyethylene glycol crosslinker. The gel formed with 10 kDa polyethylene glycol crosslinker showed the highest swelling ratio of 40 and good mechanical properties, with a storage modulus of 8 kPa. In addition, the hydrogels exhibited good biocompatibility towards both human fibroblasts and mouse monocytes, while showing strong antibacterial activity against both gram-positive and gram-negative bacteria.