Extrusion and hot compressing molding processes were used to create bio-polyethylene (BioPE) composites reinforced with argan byproducts (shell, pulp, and argan cake) as bio-fillers. The thermal stability of the composites wass analyzed by differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). Dynamical mechanical analysis and rheological testing were used to investigate their mechanical properties. The morphological results showed a good adhesion between the argan and BioPE matrix. More efficient mechanical properties have been distinguished in the case of argan byproduct-based composite. A higher Young’s modulus was noted for all the biocomposites compared to pure BioPE. Thermal analysis revealed that the addition of bio-filler to polymer reduced decomposition temperatures. This study provides an ecological alternative for upgrading the valorization of abundant and underutilized Moroccan biomass. Furthermore, the possibility of using argan byproducts in composite manufacturing will help open up new markets for what is currently considered waste.

A new eco-composite polymer for material extrusion fabrication based on fine fraction pozzolan waste was developed. In addition, the composite materials obtained were used to produce a self-watering pot with complex geometry and a permeable porous part to regulate the passage of water from the storage area to the roots of the plant. Moreover, the system was devised with a cover characterized by a UV-B barrier film. The results have shown the possibility of the 3D printing of complex geometric parts as microporous structures or thin films using a composite based on poly lactic acid (PLA) and pozzolan. The pozzolan has an effect of reinforcement for the composite and at the same time improves the cohesion between the layers of the part during printing.

An eco-friendly solution to produce new material for the material extrusion process is to use quarry waste as filler for biopolymer composites. A quarry waste that is still studied little as a filler for polymer composites is pozzolan. In this study, the optimization of the formulations and processing parameters of composites produced with pozzolan and bio-based polyethylene for 3D printing technology was performed. Furthermore, a precision irrigation system in the form of a drip watering cup was designed, printed, and characterized. The results showed that the presence of the pozzolan acted as a reinforcement for the composite material and improved the cohesion between the layers of the 3D printed objects. Furthermore, the optimization of the process conditions made it possible to print pieces of complex geometry and permeable parts for the control of the water flow rates with an order of magnitude in the range from mL/h to mL/day.