Inspired by the antifouling properties of scaly fish, the conventional silicone coating with phenylmethylsilicone oil (PSO/PDMS) composite coating was fabricated and modified with single layer polystyrene (PS) microsphere (PSO/PDMS-PS) arrays. The fish scale like micro-nano structures were fabricated on the surface of bio-inspired coating, which can reduce the contact area with the secreted protein membrane of fouling organisms effectively and prevent further adhesion between fouling organisms and bio-inspired coating. Meanwhile, PSO exuded to the coating surface has the similar function with mucus secreted by fish epidermis, which make the coating surface slithery and will be polished with the fouling organisms in turbulent waters. Compared to PSO/PDMS coating without any structure and conventional silicone coating, PSO/PDMS-PS showed better antiadhesion activity against both marine bacteria and benthic diatom (Navicula sp.). Additionally, the existence of PS microspheres can reduce the release rate of PSO greatly, which will extend the service life of coating. Compared to PSO/PDMS coating, the sustained release efficiency of PSO/PDMS-PS coating can reach 23.2%. This facile method for fabricating the bio-inspired composite slow-release antifouling coating shows a widely fabricating path for the development of synergistic anti-fouling coating.

The matching application of silicone antifouling coating and epoxy primer is a major problem in engineering. Novel epoxy-modified silicone tie-coating was prepared to tie epoxy primer and silicone antifouling coating. Firstly, N-(2-Aminoethyl)-3-aminopropyltrimethoxysilane was mechanically mixed with bisphenol A epoxy resin to form silylated epoxy resin, then the silylated epoxy resin was uniformly mixed with hydroxy-terminated polydimethylsiloxane and a curing agent and catalyst for coating. An infrared spectrometer, differential scanning calorimeter and tensile tests were used to investigate the chemical structure, phase transition temperature and mechanical properties of the tie-coatings. The interlaminar adhesion of the matching coating system was tested and analyzed by a peel-off test and a shear test. Fracture morphology was observed by scanning using an electron microscope. The results showed that crosslinking density of the tie-coating, the elastic modulus and the tensile strength of the coating increased with an increasing epoxy content, but fracture elongation decreased. The shear strength of the matching coating system is 0.37 MPa, and it shows a good tie performance. The maximum anti-peeling rate of the tie-coating on the epoxy primer reaches 100%.

In this study, we explore the effect of phenylmethylsilicone oil (PSO) addition amount and viscosity in a fouling release coating based on polydimethylsiloxane (PDMS). The surface properties, mechanical properties, anti-fouling and drag-reduction performance of the coating were studied. Meanwhile the influence of the basic properties of the coating on the anti-fouling and drag-reduction performance was also studied. Subsequently, the antifouling performance of the coating was investigated by the Navicula Tenera and bacteria adhesion test. As a result, the high content of PSO paint has a high foul removal rate. The incorporation of PSO into paint can reduce the elastic modulus and surface energy of the coating to reduce its relative adhesion factor (RAF). The lower the RAF, the better the antifouling effect of the coating. The drag-reduction performance of the coating was verified by the torque selection experiment, and the results showed that incorporation of PSO into paint can enhance the elongation and hydrophobicity of the coating, thereby increasing the drag reduction rate of the coating.

In this work, modified silicone tie-paints were prepared in a simple way for securing adhesion between the epoxy anticorrosive primer and silicone fouling release coating. Hydroxy-terminated polydimethylsiloxane (PDMS) mixture containing fillers and accessory ingredient was prepared as base component. N-(2-Aminoethyl)-3-aminopropyltrimethoxysilane (DAMO) was mechanically mixed with other functional additives as curing component. ATR-FTIR, XPS, SEM and tensile tests were used to investigate the chemical structure, morphology and mechanical properties of the tie-coatings. It was focused on the effect of the DAMO content on the adhesion of the tie-coating to epoxy primer. Peel off and shear tests were carried out to evaluate the adhesion. The results showed that introducing DAMO can significantly improve the properties of the tie-coating. The adhesion between the tie-coating and the epoxy primer increases with the increase of DAMO content, but the excessive DAMO content will decrease the fracture strength of the tie-coating and decrease the quality of the coating. When the DAMO content in tie-coating is 1.97 wt.%, the tie-coating performs excellent in the interlaminar adhesion, shear strength and mechanical properties.

Fouling-release coatings reinforced with micro-alumina and nano-alumina were prepared based on polydimethylsiloxane (PDMS) containing phenylmethylsilicone oil. The surface properties, mechanical properties, leaching behavior of silicone oil, anti-fouling and drag-reduction performance of the coating were studied. The results show that the addition of alumina can significantly improve the tensile strength, elastic modulus and Shore’s hardness of the coating. The adhesion experiments of marine bacteria and Navicula Tenera show that the addition of alumina can reduce the antifouling performance of the coating, which is related to the stripping mode of fouling organisms. The fouling organisms leave the coating surface by shearing, and the energy required for shearing is proportional to the elastic modulus of the coating. At 800–1400 rpm, the addition of alumina will reduce the drag reduction performance of the coating, which is related to the drag reduction mechanism of PDMS. PDMS counteracts part of the resistance by surface deformation. The larger the elastic modulus is, the more difficult the surface deformation is. The experiment of silicone oil leaching shows that the increase of alumina addition amount and the decrease of particle size will inhibit the leaching of silicone oil.